- Polymer Property : Tensile Strength at Break = 120 MPa
Polymer Property : Tensile Strength at Break = 120 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-2 |
| PolyOne OnForce™ LFT PP-30LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
| Ravago Manufacturing Americas Hylex® P1010G30FRMA Polycarbonate, 30% Glass Filled Polycarbonate, 30% Glass Filled, Flame RetardantInformation provided by Ravago. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
| Lanxess Durethan® BG 30 X H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, good heat-ageing resistance |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
| Lanxess Pocan® BF 4225 000000 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding, flame retardant |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | |
| LATI Latishield 66-08A G/25-V0KB1 PA66, Steel/Glass Fiber Reinforced, Flame Retardant EMI shielding product based on Polyamide 66 (PA66). Steel fibers. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Stat-kon DCL33 PC (Europe-Africa-Middle East) LNP* Stat-kon* DCL4033 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP .. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 420 PBT 30% GR, excellent strength, stiffness and dimensional stability. High heat resistance. Appliance handles, spotlights, electric motors, connectors. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® 420SE0 PBT 30% glass reinforced, UL94 V-0/5V rated. Numerous applications: edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 10% PTFE/Silicone. Added features include: Electrically Conductive. Wear Resistant, Superior Molding. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON SE003 PA 12 (Asia Pacific) LNP* Stat-kon* SE003 is a compound based on Nylon 12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp DF0069E PC LNP* Thermocomp* DF0069E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS (Asia Pacific) Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® IQNH4565 PBT (Asia Pacific) Valox* iQNH4565 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 29% based on EPEAT.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-93 |
| Wellman Wellamid® GSF25/15-66 22LH-N 40% Glass Sphere/Fiber Reinforced Nylon 66 Description: Glass Sphere/Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-93 |
| Wellman Wellamid® MRGF25/15 42H-N1/WE1705-N1 40% Mineral/Glass Fiber Reinforced Nylon 6 Description: Mineral/Glass Fiber Reinforced Nylon 6Information provided by Wellman. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-93 |
| Wellman Wellamid® MRGF3820-N 38% Mineral/Glass Reinforced Developmental Grade Nylon 66 Description: Mineral/Glass Reinforced Developmental Grade Nylon 66Information provided by Wellman. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
| DSM Akulon® M-1016 (Cond.) 33% Glass Reinforced Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® LV-3 X ESD black PA12-GF30 Grilamid LV-3 X ESD black is an antistatic Polyamide 12 for injection molding with 30% glass fiber reinforcement. Main attributes are: antistatic with resistivity < 106 Ohmgood fuel and zinc chlorid.. |
|||
| Tensile Strength at Break | 120 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec |
17400 psi @Temperature 266 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2 |
| Akro-Plastic Akromid® B3 GF 60 (2476) PA 6 Dry, 60% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2 |
| BASF Ultradur B 4300 G4 20% Glass Filled PBT Ultradur B4300 G4 is an easy flowing injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small.. |
|||
| Tensile Strength at Break | 120 MPa @Temperature 40.0 °C |
17400 psi @Temperature 104 °F |
|
| BASF Ultrason S 2010 G6 30% Glass Filled PSU Ultrason S 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO R 527 |
| Addiplast Addinyl B2 G10 V20 Nylon 6, Glass/Mineral Filled Mixed products with improved stiffness and good dimensional stability, low warpage.Information provided by Addiplast. |
|||
| Tensile Strength at Break | 120 MPa @Temperature 150 - 160 °C, Time 1.80e+7 sec |
17400 psi @Temperature 302 - 320 °F, Time 5000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® T6 GF 40 (3500) PPA Dry, 40% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
| Beijing Chemical Industry KAIFA® 301-G30 PBT Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® 70G30HSL BK039B Nylon 66
(Unverified Data**) 30% Glass Reinforced Heat Stabilized Polyamide 66 Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 120 MPa | 17400 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® TSC-10/4 EC black 9832 PA666-CF Information provided by EMS Grivory |
|||