A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP
Manufacturer A. Schulman, Inc.
Trade Name POLYPUR™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 48 hr at 80°C; ASTM D955
0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 72 hr; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Hardness, Shore D 75
75
15 sec delay; ASTM D2240
Tensile Strength, Ultimate 55.0 MPa
7980 psi
at max load; ASTM D638
Elongation at Break 100 %
100 %
ASTM D638
Elongation at Yield 4.0 %
4.0 %
ASTM D638
Flexural Modulus 2.30 GPa
334 ksi
tangent; ASTM D790
Izod Impact, Notched 0.170 J/cm
0.318 ft-lb/in
ASTM D256
0.0400 J/cm

@Temperature -40.0 °C
 0.0749 ft-lb/in

@Temperature -40.0 °F
 ASTM D256
0.0500 J/cm

@Temperature 0.000 °C
 0.0937 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C

@Thickness 3.20 mm
 185 °F

@Thickness 0.126 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C

@Thickness 3.20 mm
 167 °F

@Thickness 0.126 in
 ASTM D648