SABIC Innovative Plastics Lexan® ML6412 PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML6412 PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 260 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 260 °C |
15 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 110 % | 110 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.33 GPa | 338 ksi | 1 mm/min; ISO 527 |
| 2.50 GPa | 363 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 42.0 kJ/m² @Temperature 0.000 °C |
20.0 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 5.00 J/cm² | 23.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 75.0 J @Temperature 23.0 °C |
55.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 77.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 119 °C @Thickness 6.40 mm |
246 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 134 °C | 273 °F | Rate B/50; ISO 306 |
| 135 °C | 275 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical with Impact | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical without Impact | 100 °C | 212 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.00 mm |
V-1 @Thickness 0.0394 in |
UL 94 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 | |
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| 250 V | 250 V | IEC 60112 | |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Chevron Phillips Marlex® HHM TR-480Z/M362 Natural high density ethylene hexene copolymer/black concrete (disc
- LNP Thermocomp® GF-1006 Polysulfone, Glass Fiber Reinforcement (discontinued **)
- KB Alloys Ticar® 5% Ti - 0.18% C Titanium Carbon Aluminum Rod
- SABIC Innovative Plastics Ultem SF2250 PEI Blend (Europe-Africa-Middle East)
- Daikin NEOFLON NC-1539 FEP Coating Powder, Gray
- Arlon 45NK Woven Kevlar® Reinforced Laminate and Prepreg
- Techmer ES HiFill FR® PA6/6 GF20 FR 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved