Polymer Property : Flexural Yield Strength = 95.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® CE1821 PC+ABS
High stiffness PC/ABS blend offering high impact, high heat, low CTE, good surface quality and excellent extrusion and thermoforming characteristics.
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CY5000 PC+ABS (Asia Pacific)
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS
Cycoloy CY6010 resin is a flame retardant PC/ABS blend featuring excellent flow together with good impact and UL-94 V0 listing at 1.5mm. Its excellent flow combined with balanced heat and good pract..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® XCM830 PC+ABS
PC/ABS with high stiffness and impact performance
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 500ECR PC (Europe-Africa-Middle East)
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 503R PC (Europe-Africa-Middle East)
LEXAN 503R is a medium viscosity, 10% glass reinforced, UV-stabilized, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance and exce..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 505R PC (Asia Pacific)
Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm...
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® EX1332T PC (Europe-Africa-Middle East)
LEXAN* EX1332T polycarbonate resin, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, extrusion, mold release, UV stabilized, transparent, translucent and opaque colors. Multiwall sheet, Profi..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer
Lexan* EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent ..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer (Europe-Africa-Middle East)
Lexan* EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high fl..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EXL4419 PC Copolymer (Asia Pacific)
Lexan* EXL4419 polycarbonate (PC) siloxane copolymer resin is a 9% Glass Fiber (GF) reinforced opaque injection molding (IM) grade. This medium flow resin offers much higher ductility, improved rele..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Lexan® HPH4504 PPC
High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 of USP Class VI). EtO, steam, gamma and e-beam steril..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HPS7R PC (Europe-Africa-Middle East)
Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. ..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® ML6411 PC Copolymer (Europe-Africa-Middle East)
Lexan* ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® PK2870 PC (Asia Pacific)
LEXAN* PK2870 polycarbonate resin, global grade, MVR (300C/1.2kg) 2 cm3/10min, high viscosity, branched, blow molding, high melt strength, high impact resistance, Available in transparent colors onl..
Flexural Yield Strength 95.0 MPa

@Temperature 90.0 °C
13800 psi

@Temperature 194 °F
ISO 178, ASTM D790
Nilit Nilamid B G6 FR HF 30% Glass Fiber Reinforced, Flame Retardant PA6
Description: Nilamid B G6 FR HF is a NYLON 6 based flame retardant compound that does not contain any halogen or red phosphorous. It has a good overall mechanical performance, has an excellent price..
Flexural Yield Strength 95.0 MPa
13800 psi
Plain Cast Resin; ASTM D790
TSE Industries EcoWIND® T211 Filament Winding Polyurethane Resin for Tanks and Pressure Vessels with Thermoplastic Liners
TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® re..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4271 PC (Asia Pacific)
Lexan* HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271 has enhanced mold release, impact ductility..
Flexural Yield Strength 95.0 MPa
13800 psi
Ineos Barex® 210 E Acrylonitrile-Methyl Acrylate Copolymer
Extrusion Grade. Barex® Resins are available in either natural or blue tint. Barex® 210E is most commonly used for thermoformed sheet applications.
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Europe-Africa-Middle East)
Low flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change (MoC), biocompatible (ISO 10993 or USP Class VI)..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER
Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), fo..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER (Europe-Africa-Middle East)
Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), fo..
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Europe-Africa-Middle East)
PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP C7410 PC+ABS (Asia Pacific)
LNP* Thermocomp* C7410 compound is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications.
Flexural Yield Strength 95.0 MPa
13800 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA (Asia Pacific)
Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX934 PPE+PA (Asia Pacific)
NORYL GTX934 is an unfilled GTX grade with improved processability and heat ageing performance.
Flexural Yield Strength 95.0 MPa
13800 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX626 PPE+PS+PA
Blowmolding and extrusion. High heat and chemical resistant.
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Asia Pacific)
Noryl GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be..
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Europe-Africa-Middle East)
Noryl GTX678 resin is a high performance blend of PPE/PA that exhibits an excellent balance on non-halogenated flame retardance, conductivity, ductility, and high-heat resistance. This grade can be..