Polyram RamOfin PPH353M8 Polypropylene, 40% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH353M8 Polypropylene, 40% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% mineral filled polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.750 J/cm @Temperature 23.0 °C |
1.41 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Albis Plastics Cellulose Acetate CA700 , Unreinforced, 29% Plasticizer (discontinued **)
- LATI Latilub 62-01M G/30 PA6, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP UFL36SXP PPA (Europe-Africa-Middle East)
- Saint-Gobain Rulon® 1410 Grade Bearing/Seal PTFE
- Styron MAGNUMâ„¢ 8391 Acrylonitrile Butadiene Styrene (ABS) Resin
- SABIC Innovative Plastics Ultem 1010KM PEI
- Eagle Brass 706 Copper Nickel 10%, Hard
- EMS-Griltech Griltex® 1A Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- A. Schulman ComAlloy Comshield® 104 Homopolymer Polypropylene, Electrically Conductive - Carbon Black Filled
Copyright © lookpolymers.com All Rights Reserved