Polymer Property : Tensile Strength, Yield = 62.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Cycoloy® CY5105 PC+ABS (Europe-Africa-Middle East)
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering excellent flow / impact balance for large size applicationsThis data was supplied by SABIC-IP ..
Tensile Strength, Yield 62.0 MPa
8990 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Geloy HRA222 ASA (Europe-Africa-Middle East)
GELOY HRA222 is a multi-purpose, chlorine and bromine free flame retardant ASA+PC alloy for injection moulding processes. Typical properties as measured on natural material.This data was supplied by..
Tensile Strength, Yield 62.0 MPa
8990 psi
5 mm/min; ISO 527
SABIC Innovative Plastics GELOY HRA222F ASA+PC (Europe-Africa-Middle East)
Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant ASA-PC alloy for injection moulding processes. This grade has a F1 rating according UL746C. Typical properties as measured..
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 123 PC
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 17.5 MFR, for small, intricate parts. UV stabilized.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 203 PC (Asia Pacific)
7.0 MFR, for thicker sections without sinks. Improved flame retardance. UV stabilized for outdoor and lighting.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 223S PC (Asia Pacific)
17.5 MFR, for small, intricate parts. Improved flame retardance. Internal mold release. UV stabilized.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 923 PC (Asia Pacific)
Opaque colors, low viscosity, superior flame retardance. Decreased smoke and lowered toxic gas emission. UV-stabilized.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 923A PC
Low viscosity, flame retardant with exceptional surface. Clear, tints and opaque colors. UV-stabilized.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 943A PC
Medium viscosity, superior flame retardance. UV-Stabilized. Clear, tints and opaque colors.
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® BFL2010 PC
Non-brominated, non-chlorinated flame retardant, glass reinforced PC with improved flow. Available in opaque colors.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® FXD103R PC (Asia Pacific)
FXD103R is a Light Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect propert..
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer (Europe-Africa-Middle East)
18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPS1R PC (Asia Pacific)
High flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, e-beam and gamma sterilizable. Contains..
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPS7 PC (Europe-Africa-Middle East)
Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. ..
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® LUX2180T_ PC (Europe-Africa-Middle East)
Global grade. LEXAN LUX2180T is an injection moulding grade especially designed for manufacturing optical parts requiring easy flow properties combined with very high transmission and color stabilit..
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® ML7691 PC
UV stabilized clear polycarbonate formula for internal uses only.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C2801 PC+ABS
LNP* Lubricomp* Cycoloy_C2801 compound is a 5% PTFE reinforced PC+ABS, wear resistant, flame retardant compound for moving components in business equipment. Medium heat performance
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 143 PC (Asia Pacific)
Nonhalogenated. 10.5 MFR. UV-stabilized.
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 9925A PC (Asia Pacific)
Lexan 9925A is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance. It intended to meet WEEE/RoHS requireme..
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HF1110R PC (Asia Pacific)
High flow grade. Easy mold release version of LEXAN HF1110. For thin wall lighting lenses, data storage components and safety eyewear lenses.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HP2 PC (Asia Pacific)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m..
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HP2NR PC (Asia Pacific)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no..
Tensile Strength, Yield 62.0 MPa
8990 psi
ASTM D638
LG Chemical Lupox® GP-1001F General Purpose PBT, Unreinforced, Flame Retardant
LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho..
Tensile Strength, Yield 62.0 MPa
8990 psi
ASTM D638
LG Chemical LUPOY GP-1006F General Purpose Modified PC, Unreinforced, Weather Resistant, Flame Retardant
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527-1,-2
Covestro Bayblend® M850 XF PC/ABS Blend
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Injection molding• Eas..
Tensile Strength, Yield 62.0 MPa
8990 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® EXRL0681 PC Copolymer
25 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® FXE144H PC (Europe-Africa-Middle East)
FXE144H is a Lexan PC Translucent Grade in our VisualFX Portfolio. It is part of Energy family, which includes Illuminate, Glass, and Flame effects. Grade was developed to meet the Aesthetic Differe..
Tensile Strength, Yield 62.0 MPa
8990 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WF002I PBT
LNP* THERMOTUF* WF006I is a compound based on PBT resin containing 10% Glass Fiber. Added feature of this grade is: High Impact.