SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* KL001 is a compound based on Acetal Copolymer resin containing 5% PTFE. Added feature of this material is: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/inÂ³	ISO 1183
	1.44 g/cc	0.0520 lb/inÂ³	ASTM D792
Moisture Absorption	0.200 %	0.200 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955
	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ASTM D955
	0.023 cm/cm @Time 86400 sec	0.023 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	52.0 MPa	7540 psi	ASTM D638
	53.0 MPa	7690 psi	ISO 527
Tensile Strength, Yield	54.0 MPa	7830 psi	ISO 527
	55.0 MPa	7980 psi	ASTM D638
Elongation at Break	29.6 %	29.6 %	ISO 527
	33.9 %	33.9 %	ASTM D638
Elongation at Yield	9.8 %	9.8 %	ASTM D638
	11.4 %	11.4 %	ISO 527
Tensile Modulus	2.62 GPa	380 ksi	1 mm/min; ISO 527
	2.75 GPa	399 ksi	50 mm/min; ASTM D638
Flexural Strength	13.0 MPa	1890 psi	ASTM D790
	70.0 MPa	10200 psi	ISO 178
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
	3.44 GPa	499 ksi	ASTM D790
Izod Impact, Notched	0.0500 J/cm	0.0937 ft-lb/in	ASTM D256
Izod Impact, Unnotched	0.640 J/cm	1.20 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	47.0 kJ/mÂ²	22.4 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	1029 kJ/mÂ²	489.6 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	5.00 J	3.69 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic	0.38	0.38	ASTM D3702 Modified
Coefficient of Friction, Static	0.17	0.17	ASTM D3702 Modified
K (wear) Factor	44.3 x 10^-8 mmÂ³/N-M	22.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	118 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	65.6 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	119 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	66.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	113 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	62.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	113 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	62.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	149 Â°C	300 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	157 Â°C @Thickness 3.20 mm	315 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	96.0 Â°C	205 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	112 Â°C @Thickness 3.20 mm	234 Â°F @Thickness 0.126 in	unannealed; ASTM D648