- Polymer Property : Melt Index of Compound = 15 g/10 min
Polymer Property : Melt Index of Compound = 15 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound |
15
-
16
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
-
16
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238 |
|
Ovation Polymers RIGITRON 10030 GF Polycarbonate, 30% Glass Reinforced
PC - Glass reinforced (30 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polykemi AB POLYfill PP CIQ15020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polykemi AB POLYfill PPH 150DNH Polypropylene Homopolymer, Flame Retardant, Halogen Free
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 260 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 500 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS (Europe-Africa-Middle East)
Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.4mm and 5VB at 1...
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 260 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 500 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Asia Pacific)
Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polykemi AB POLYfill PPH TS15010 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 260 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 500 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics GELOY HRA150 ASA (Europe-Africa-Middle East)
GELOY HRA150 is a high heat resistant ASA+PC. GELOY HRA150 shows high impact retention and color stability upon weathering, and hence can be positioned in various outdoor and indoor applications req..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® EXL9134 PC Copolymer
Lexan* EXL9134 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, ..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 260 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 500 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® ML6412 PC Copolymer
ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system.
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F
|
ASTM D1238 |
|
LG Chemical LUCEL N115 POM, Unreinforced, High Viscosity
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 260 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 500 °F
|
ASTM D1238 |
|
Mitsui APELâ„¢ APL6013T Cyclo Olefin Copolymer (COC)
This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt proces..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 10.0 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 22.0 lb,<br> Temperature 572 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL V03550 PPE+HIPS (Asia Pacific)
Noryl* V03550 is a 35% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 340 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 644 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer
High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 250 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 482 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQNH4550 PBT (Asia Pacific)
Valox* iQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% based on EPEAT..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 250 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 482 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® VIC4311 PBT
VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 572 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics LNP THERMOCOMP 9X10312 PA (Asia Pacific)
9X10312 is 50% glass fiber reinforced, impact modified nylon material. High modulus, high flow and good ductility, Low Moisture Absorption.
|
|||
| Melt Index of Compound | 15 - 20 g/10 min | 15 - 20 g/10 min | I Preparation |
|
Sibur ABS-TB (30,31) Molding Grade ABS Plastic
With high fluidity of melting, thermal and light resistance for large parts of devices, parts of refrigerators, and for hearing aids. Mark is allowed for contact with food products.
|
|||
| Melt Index of Compound |
15
-
20
g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C
|
15
-
20
g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F
|
ASTM D1238 |
|
Shinkong Synthetic Fibers Shinite® D201K008 PBT, High Viscosity
Information from Shinkong Synthetic Fibers Corp.
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 280 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 536 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66
NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting.
|
|||
| Melt Index of Compound |
15
-
20
g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C
|
15
-
20
g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F
|
ASTM D1238 |
|
Shinkong Synthetic Fibers Shinite® D201K008 PBT, High Viscosity
Information from Shinkong Synthetic Fibers Corp.
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 280 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 536 °F
|
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL N1150 PPE+PS (Europe-Africa-Middle East)
Noryl* N1150 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow, this resin also uses non-chlorinated, non-brominated FR add..
|
|||
| Melt Index of Compound |
15
-
25
g/10 min <br>@Load 5.00 kg,<br> Temperature 265 °C
|
15
-
25
g/10 min <br>@Load 11.0 lb,<br> Temperature 509 °F
|
|
|
3M Dyneon™ FX 5912 Dynamar™ Polymer Processing Additive
Dynamar FX 5912 is a free-flowing fluorothermoplastic processing aid that is designed for use at very low levels to improve the processing of thermoplastics. Typical use levels of 200 to 1000 ppm ha..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 372 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 702 °F
|
ASTM D1238 |
|
3M Dyneon™ PFA FLEX 8515 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules
Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this f..
|
|||
| Melt Index of Compound | 15 g/10 min | 15 g/10 min | ASTM D1238 |
|
Cheng Yu Plastic 3235 TPE Rubber |
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 372 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 702 °F
|
ASTM D1238 |
|
3M Dyneon™ PFA 6515NZ Perfluoroalkoxy Fluorothermoplastic
PFA designed for higher speed or higher shear processing such as injection molding and wire insulation. Demonstrates universal chemical and solvent resistance, high dielectric strength, excellent we..
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
A.D. Compound Adene NTFA Homopolymer 20% Talc Filled Polypropylene
Information provided by A.D. Compound
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polykemi AB POLYfill PPH TS15030 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
A.D. Compound Adene NCHA Homopolymer 25% CaCO3 Filled Polypropylene
Information provided by A.D. Compound
|
|||
Copyright © lookpolymers.com All Rights Reserved