- Polymer Property : Melt Index of Compound = 15 g/10 min
Polymer Property : Melt Index of Compound = 15 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound |
15
g/10 min @Load 10.0 kg, Temperature 220 °C |
15
g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Cycolac® MGABS01 ABS
Injection molding ABS. High impact, high gloss, good flow.
|
|||
| Melt Index of Compound |
15
g/10 min @Load 5.00 kg, Temperature 260 °C |
15
g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
|
Polykemi AB POLYblend 85H PC/ABS-Blend
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 230 °C |
15
g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
|
Polykemi AB POLYfill PPC TS15020E Polypropylene Copolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 260 °C |
15
g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS
Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.2mm and 5VB at 1...
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 260 °C |
15
g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS
Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 230 °C |
15
g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
|
Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min @Load 1.20 kg, Temperature 300 °C |
15
g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® EXL9134 PC Copolymer (Asia Pacific)
Lexan* EXL9134 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, ..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 1.20 kg, Temperature 300 °C |
15
g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Lexan® EXL9134 PC Copolymer (Europe-Africa-Middle East)
Lexan* EXL9134 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, ..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 5.00 kg, Temperature 372 °C |
15
g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
|
3M Dyneon™ PFA 6515N Perfluoroalkoxy Fluorothermoplastic
(discontinued **)
The excellent chemical temperature resistance of Dyneon™ 6500N PFA is available across a range of melt flow indices, for optimal processability. Dyneon™ PFA 6502N, the highest molecular weight gra..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 190 °C |
15
g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
|
LG Chemical LUCEL N115 POM, Unreinforced, High Viscosity
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 3.80 kg, Temperature 280 °C |
15
g/10 min @Load 8.38 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL SE0 PPE+HIPS (Europe-Africa-Middle East)
NORYL SE0 is an unfilled, flame retardant material with a Vicat B/120 of 130C according ISO 306. NORYL SE0 is V0 at 1.6 mm according UL94 and halogen free according VDE/DIN 472 part 815.
|
|||
| Melt Index of Compound |
15
g/10 min @Load 10.0 kg, Temperature 300 °C |
15
g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL V03550 PPE+HIPS
Noryl* V03550 is a 35% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 10.0 kg, Temperature 300 °C |
15
g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL V03550 PPE+HIPS (Europe-Africa-Middle East)
Noryl* V03550 is a 35% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 265 °C |
15
g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific)
VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 5.00 kg, Temperature 250 °C |
15
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Valox® IQNH4550 PBT (Asia Pacific)
Valox* iQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% based on EPEAT..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 5.00 kg, Temperature 250 °C |
15
g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Xenoy® 5220U PBT+PC
Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance.
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 265 °C |
15
g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics XYLEX HX8300HP PC+POLYESTER
Medium flow, Transparent PC/Polyester alloy. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant...
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 300 °C |
15
g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics LNP THERMOCOMP EXTC8143 PC (Asia Pacific)
LNP* Thermocomp* EXTC8143 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, No..
|
|||
| Melt Index of Compound |
15
-
20
g/10 min @Load 2.16 kg, Temperature 250 °C |
15
-
20
g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
|
Shinkong Synthetic Fibers Shinite® D201K008 PBT, High Viscosity
Information from Shinkong Synthetic Fibers Corp.
|
|||
| Melt Index of Compound |
15
g/10 min @Load 10.0 kg, Temperature 280 °C |
15
g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL GFN2V PPE+HIPS (Europe-Africa-Middle East)
NORYL GFN2V is a 20 % glass fibre reinforced material with a HDT/A of 130C according ISO 75. NORYL GFN2V cust spec 1977 has been approved for potable water applications up to 85C by the UK WFBS acco..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 5.00 kg, Temperature 280 °C |
15
g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific)
Noryl* EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR a..
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 265 °C |
15
g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Europe-Africa-Middle East)
PC+Polyester, UV Stabilized, Transparent
|
|||
| Melt Index of Compound | 15 - 20 g/10 min | 15 - 20 g/10 min | ASTM D1238 |
|
Cheng Yu Plastic PP230H TALC 30 Polypropylene, 30% Talc, High Heat |
|||
| Melt Index of Compound |
15
-
20
g/10 min @Load 1.20 kg, Temperature 300 °C |
15
-
20
g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238, ISO 1133 |
|
EPICHEM Epilon PC IX3000 Polycarbonate, High Impact
Characteristics: high fluidity, high impact
|
|||
| Melt Index of Compound | 15 g/10 min | 15 g/10 min | ASTM D1238 |
|
Cheng Yu Plastic 3213 TPE Rubber |
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 230 °C |
15
g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
|
A.D. Compound Adene NCFA Homopolymer 20% CaCO3 Filled Polypropylene
Information provided by A.D. Compound
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 230 °C |
15
g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
|
Polykemi AB POLYfill PP 150ENH Polypropylene, Flame Retardant, Halogen Free
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 230 °C |
15
g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
|
Polykemi AB POLYfill PPH TS15030 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min @Load 2.16 kg, Temperature 230 °C |
15
g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
|
Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Melt Index of Compound |
15
g/10 min @Load 5.00 kg, Temperature 265 °C |
15
g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
|
SABIC Innovative Plastics Xenoy® X5630P PET+PC (Europe-Africa-Middle East)
Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications
|
|||