SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistance. Excellent flow and impact balance together with the thin wall flame resistance and all color options make Cycoloy CX7240U an ideal candidate for a wide variety of thin wall applications.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 2.16 kg,
Temperature 260 °C
16 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 260 °C
15 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Break 90 %
90 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
4.1 %
4.1 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.53 GPa
367 ksi
1 mm/min; ISO 527
2.95 GPa
428 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 96.0 MPa
13900 psi
2 mm/min; ISO 178
104 MPa
15100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.75 GPa
399 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.00 J/cm
9.37 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 65.0 J

@Temperature 23.0 °C
47.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 62.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
62.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 53.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
54.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 100 °C

@Thickness 3.20 mm
212 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
89.0 °C

@Thickness 3.20 mm
192 °F

@Thickness 0.126 in
unannealed; ASTM D648
99.0 °C

@Thickness 6.40 mm
210 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 106 °C
223 °F
Rate B/50; ASTM D1525
110 °C
230 °F
Rate B/50; ISO 306
113 °C
235 °F
Rate B/120; ISO 306
UL RTI, Electrical 90.0 °C
194 °F
UL 746B
UL RTI, Mechanical with Impact 90.0 °C
194 °F
UL 746B
UL RTI, Mechanical without Impact 90.0 °C
194 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
UL 94
V-1

@Thickness 0.600 mm
V-1

@Thickness 0.0236 in
UL 94
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94
5VB

@Thickness 1.50 mm
5VB

@Thickness 0.0591 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Glow Wire Test 800 °C
1470 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2