- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 89.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 89.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 6.40 mm |
192
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS
Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffnes..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific)
Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Europe-Africa-Middle East)
Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX2244ME PC+ABS
Cycoloy* CX2244ME resin is a flame retardant PC/ABS blend featuring excellent balance of flow and impact together with UL-94 V0 rating at < 1mm. Cycoloy CX2244ME resin also demonstrates improved che..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX7211 PC+ABS
Cycoloy* CX7211 PC/ABS resin is a non-filled, injection moldable grade which has UL 94 rating at 2.5 mm 5VA. Cycoloy CX7211 resin provides all color options and features an excellent balance of flo..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX7240 PC+ABS (Europe-Africa-Middle East)
Cycoloy* CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.4mm and 5VB at 1...
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS
Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Europe-Africa-Middle East)
Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics GELOY FXW751SK ASA+PC (Asia Pacific)
Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact Resin
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Geloy FXW751SK ASA+PC (Europe-Africa-Middle East)
Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact ResinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
|
PTS SAN-80HF High Flow SAN Resin
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX2244ME PC+ABS (Asia Pacific)
Cycoloy* CX2244ME resin is a flame retardant PC/ABS blend featuring excellent balance of flow and impact together with UL-94 V0 rating at < 1mm. Cycoloy CX2244ME resin also demonstrates improved che..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics GELOY CR7500 ASA (Europe-Africa-Middle East)
High heat ASA with optimum flow-impact balance. For Automotive applications and Automotive colors only.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 - 177 °C | 192 - 350 °F | Average value: 149 °C Grade Count:38 |
|
Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% ar..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East)
LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 6.40 mm |
192
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical RS800M ABS, High Modulus, Chemical Resistance to HCFC
Feature: Extrusion Molding, High Modulus, Chemical Resistance to HCFCApplication: Refrigerator Inner LinerCAS No. 9003-56-9Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ISO 75A |
|
Lucite International Diakon® CLG960 Acrylic Polymer
Information provided by Lucite International
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | 80*10*4mm, Cut; ISO 75-1&2 |
|
SABIC Innovative Plastics SABIC PPCOMPOUND 19T1040 PP
SABIC® PPcompound 19T1040 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Lubriloy D20001 PC
LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.This data was supplied by..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 3.20 mm |
192
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRILOY D20001 PC (Asia Pacific)
LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Xenoy® X5300WX PBT+PC
Unreinforced, opaque PBT+PC alloy. Chemical resistance and good mechanical performance. UV-stabilized. Excellent weatherability.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-LOY 9X07438 ASA+PC
LNP* STAT-LOY* 9X07438 is a compound based on Polycarbonate/ASA containing Proprietary Filler(s). Added features of this grade include: Antistatic, Colorable, Weatherable.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 6.40 mm |
192
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Infino® NH-1021 PC/ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 6.40 mm |
192
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® ES-0173 ABS, Extrusion Grade
Extrusion ABS for the interior of refrigerator with HCFC-141b, down gauging characteristicInformation provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
89.0
°C @Thickness 6.40 mm |
192
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® LX-0970 LS ABS, Unreinforced Metallic-Look
Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics NORYL PVX0901 PPE+PS (Asia Pacific)
Multi purpose V1 grade
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | 0.5 inch; ASTM D648 |
|
PlastxWorld CEVIAN®-V 500 ABS
Medium Impact ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | unannealed; ISO 75 |
|
Chi Mei Polylac® PA-756 ABS - High Flow
High rigid, high flow
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | unannealed; ISO 75 |
|
Chi Mei Polylac® PA-756H ABS - High Flow
Super high flow
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
|
Beijing Chemical Industry KAIFA® GL1200 ABS General Purpose Grade
Middle impact, Good mechanical strength, High flexural strengthInformation provided by Beijing Chemical Industry Research Institute (Group)
|
|||