RheTech Products T40P100-04 40% Talc Reinforced Polypropylene, White
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products T40P100-04 40% Talc Reinforced Polypropylene, White.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive componentsConsumer productsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 40 % | 40 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0095 cm/cm | 0.0095 in/in | ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 28.3 MPa | 4100 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 3.62 GPa | 525 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm @Temperature 23.0 °C |
0.400 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 1.13 J | 0.830 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Middle Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Front Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Nozzle Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP Lubricomp DBL14 PC (Europe-Africa-Middle East)
- Techmer ES HiFill® ABS GF30 BK 30% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC
- Samsung Cheil Industries Infino® HA-1011 PC/ABS, Unreinforced
- Lubrizol Estane® R190A Thermoplastic Polyurethane
- Chosun Refractories APC-50G Acid-proof Castable
- Dow DOWLEX™ 2045.02AC Linear Low Density Polyethylene, Blown Film Grade
- Fainplast Compounds PH 80 Flexible PVC, Transparent Extrusion
- Asahi Kasei Thermylene® P7-30FG-0874 30% Glass Fiber Reinforced, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved