Tra-Con Tra-Bond F131 High Tg Room Temperature Cure Fiber Optic Adhesive

Category	Polymer , Adhesive , Thermoset , Epoxy
Manufacturer	Tra-Con, Inc.
Trade Name	Tra-Bond
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tra-Con Tra-Bond F131 High Tg Room Temperature Cure Fiber Optic Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TRA-BOND F131 is a fiber-optic adhesive used for terminating ALL types of fiber-optic connectors as well as LED displays, lenses and other optical components. It produces a typical Tg of 95°C thus meeting specification requirements of Bellcore and connector manufacturers. This two-part, low viscosity system can be cured at room temperature overnight or as fast as 15 minutes at 65°C. Information provided by Tra-Con Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	Mixed
Viscosity	1800 cP @Temperature 25.0 °C	1800 cP @Temperature 77.0 °F	After mixing

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	78	78
Adhesive Bond Strength	25.5 MPa	3700 psi	Lap shear, alum to alum
Izod Impact, Notched	0.117 J/cm	0.220 ft-lb/in

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	120 °C	248 °F
Minimum Service Temperature, Air	-60.0 °C	-76.0 °F
Glass Transition Temp, Tg	95.0 °C	203 °F	Ultimate Tg

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 90.0 °C	0.250 hour @Temperature 194 °F	1 drop applications
	60.0 min @Temperature 65.0 °C	1.00 hour @Temperature 149 °F
	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F

Descriptive Properties	Value	Comments
Color	Clear	Mixed
Mix Ratio, parts by weight	100/30	Resin/Hardener
Thixotropic Index	1