- RheTech Products F55-01 43% Glass Fiber/Talc Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black
RheTech Products F55-01 43% Glass Fiber/Talc Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products F55-01 43% Glass Fiber/Talc Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Consumer goodsSupportsGolf cart bracketsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 43 % | 43 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength at Break | 75.8 MPa | 11000 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 6.76 GPa | 980 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.339 J | 0.250 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Middle Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Front Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Nozzle Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV 1197 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Chevron Phillips Vytek™ V205C3 Enhanced LLDPE Blown Film Resin (discontinued **)
- Mallard Creek Polymers ROVENE® 5005 SBR Latex
- Materion Beryllium Copper Alloy 10 Rod and Bar; A (TB00) Temper; All Sizes (UNS C17500)
- LG Chemical SHP-IPA ISOPROPYL ALCOHOL
- Techmer ES HiFill® PA6 GF33 L BK001 33% Glass Filled
- A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 93A
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.5 PHR Sulfur
- Ascend Performance Materials Vydyne® 75HF Nylon 66/6, Heat Stabilized, DAM
Copyright © lookpolymers.com All Rights Reserved