- RheTech Products F37-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
RheTech Products F37-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products F37-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: ElectronicsBracketsBattery traysInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 40 % | 40 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | ASTM D2240 |
| Tensile Strength at Break | 53.8 MPa | 7800 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 5.69 GPa | 825 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 23.0 °C |
0.800 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.451 J | 0.333 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 312 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Middle Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Front Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Nozzle Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Silicon Iron FS-1601 Powdered Metal
- Michelman® Michem® Prime 4983R Ethylene acrylic acid dispersion
- Silon Tabond 3042 Impact Modifier for PA
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 50 PHR N990 (MT) Filler
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N220 Filler
- Hippe PBT Polybutylene Terephthalate
- 3M S38 Glass Bubbles
- ATI Allvac® Nickelvac® 625 Nickel Superalloy, Heat Treatment: 927°C (1700°F) Anneal
- PolyOne Stat-Tech™ PI-05CF/000 EM Polyetherimide (PEI) (discontinued **)
- Zircar Zirconia ZR-RIG Zirconia Rigidizer
Copyright © lookpolymers.com All Rights Reserved