- Eurostar Staramide BG6ST01 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
Eurostar Staramide BG6ST01 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide BG6ST01 PA6, Glass Fiber Filled, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide BG6ST01 is an Impact Modified and Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 138 MPa | 20000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.90 GPa | 1150 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
48.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 240 - 260 °C | 464 - 500 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 3201-xx05D Polyvinyl Chloride, Flexible (PVC, Flexible)
- Michelman® Licomer® T 51 Acrylic copolymer dispersion
- Teknor Apex APEX® 121 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific)
- Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/42%/48370/1000
- Eastman Tenite 350A4861313 Cellulose Acetate Propionate, Clear, Trsp
- Dow AFFINITY™ GA 1900 Polyolefin Plastomer (POP)
- Eurostar Staramide PFB24 PA6, 15% Glass Fiber, 15% Glass Bead Filled, Injection Molding Resin
- Braskem TI4350P Impact Copolymer Polypropylene
- Arlon 18986XA023 0.023" Uncured/Cured Silicone Rubber with Fiberglass Substrate