Polymer Resources NY66-IM2 Impact Modified Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources NY66-IM2 Impact Modified Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 66, Superior Impact Modified, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.3 MPa | 7300 psi | ASTM D638 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 1.69 GPa | 245 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm @Temperature 22.8 °C |
16.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
UL 746 |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
UL 746 |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
UL 746 |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Middle Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Front Barrel Temperature | 277 - 288 °C | 530 - 550 °F | |
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 73.9 - 85.0 °C | 165 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0003 |
Users viewing this material also viewed the following:
- RheTech Products FRG130-01 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Flame Retardant, Black
- SABIC Innovative Plastics SABIC STAMAX 30YM240 PP
- SABIC Innovative Plastics Valox® IQ420 PBT (Europe-Africa-Middle East)
- Sax Polymers SAXAMID 126F7 Nylon 6, 35% Glass Fiber
- Tipco Tipcolite® TPF 1512 Phenolic Resin having 680 cps Viscosity containing 68% Solids
- DuPont Performance Polymers Zytel® FR70M30V0 NC010 Nylon 66 (Unverified Data**)
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, Hardness 70A
- Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, at 50% RH (di
- Polyram RamTough PZ304G2 Polycarbonate, 10% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved