SABIC Innovative Plastics Lexan® OQ2220 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® OQ2220 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent production control conditions.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 17.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
17.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 125 % | 125 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 6.94 J/cm @Temperature 23.0 °C |
13.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 7.30 J/cm² @Temperature 23.0 °C |
34.7 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Tensile Impact Strength | 472 kJ/m² | 225 ft-lb/in² | Type S; ASTM D 1822 |
| Impact Test | 62.0 J @Temperature 23.0 °C |
45.7 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C @Thickness 6.40 mm |
264 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D 542 |
| Haze | 0.60 % @Thickness 2.54 mm |
0.60 % @Thickness 0.100 in |
ASTM D 1003 |
| Yellow Index | 0.00 % | 0.00 % | ASTM D 1925 |
| Transmission, Visible | 89 % @Thickness 2.54 mm |
89 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 6208 BLK
- SABIC 120W Linear Low Density Polyethylene for Blown Film
- Fluorseals PTFE 60% bronze filled
- Mi-Tech Metals CW68 68 Tungsten/32 Copper PM Metal Composite
- Stir SpA Giesse RSA/8 (PVC)
- A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene
- Chi Mei Kibisan® PN-117C SAN
- ExxonMobil Spartan EP 680
- AK Steel ASTM A 907, Grade 40 Hot Rolled Carbon Steel, Structural Quality (SQ)
- BASF Capron® 8232G HS FR 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved