- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 213 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 213 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 |
|
Polymer Resources NY66-IM2-[color]H Nylon, Superior Impact Modified, Heat Stabilized (DAM)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP EFL24P PEI
LNP* LUBRICOMP* EFL24P is a compound based on Polyetherimide resin containing 20% Glass Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Exceptional Processing.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP EX03647H PEI
LNP LUBRICOMP* EX03647H is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 6.40 mm |
415
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 2412EPR PEI (Asia Pacific)
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the As..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM CRS5011R PEI
Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM UF5011S PEI (Asia Pacific)
Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Stat-kon EE002ER PEI (Europe-Africa-Middle East)
LNP* Lubricomp* EFP36G is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive.This data wa..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF15 L 15% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: LubricantFeatures: LubricatedProcessing Method: Injection MoldingInformation ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF15 L UV BK 15% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: UV Stabilizer and LubricantFeatures: Good UV Resistance and LubricatedAppeara..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF18 HS L 18% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 18% Filler by Weight Additive: Lubricant and Heat StabilizerFeatures: Heat Stabilized and LubricatedInformat..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF20 HS L BK 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Additive: Lubricant and Heat StabilizerFeatures: Heat Stabilized and LubricatedAppearan..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6 GF20 L UV 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Processing Method: Injection MoldingInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Thermocomp EF008EXP PEI (Europe-Africa-Middle East)
LNP* Thermocomp* EF008EXP is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SABIC-IP ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP IF006 PA 6/12
LNP THERMOCOMP* IF006 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific)
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM JD4901 PEI (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS
LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 |
|
Plastics Group Polifil® 627L Nylon 6/6 (DAM)
Polifil® NYLON 6/6 combines good abrasion and chemical resistance.Applications: ValvesBearingsBearing casesStandard processing techniques are applicable. Information provided by The Plastics Group...
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
213
°C @Thickness 3.20 mm |
415
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
|
|||