Polymer Property : Linear Mold Shrinkage = 0.017 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage	0.017 - 0.024 cm/cm	0.017 - 0.024 in/in	Across Flow; ISO 2577
Polykemi AB POLYelast TPE Z400 Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB
Linear Mold Shrinkage	0.017 - 0.024 cm/cm	0.017 - 0.024 in/in	With Flow; ISO 2577
Polykemi AB POLYelast TPE Z600P Thermoplastic Elastomer, SEBS-based, Co-injection, PA-adhesion Information provided by Polykemi AB
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	Across Flow; ISO 2577
Polykemi AB SCANAMID 66 A13^ Q2 EX8 Nylon 66, Mineral Reinforced Information provided by Polykemi AB
Linear Mold Shrinkage	0.017 cm/cm @Thickness 80.0 mm	0.017 in/in @Thickness 3.15 in	sheet; ASTM D4894
3M Dyneon™ TF 4105 PTFE 25% Glass Fiber Filled (discontinued **) Type II PTFE. Applications include valve seats, bearings, seals/gaskets, moldings, piston rings.Data provided by Dyneon.
Linear Mold Shrinkage	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in	ASTM D955
LG Chemical LUCEL FW-715C Friction and Wear Resistant POM, Polymeric Wear Additive, CaCo3 Filled, Low Warpage, Antistatic LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage	0.017 - 0.023 cm/cm	0.017 - 0.023 in/in	ASTM D955
Kolon SPESINÂ® KP270 General Purpose PBT Base Resin Excellent extrudabilityApplications: CablesInformation provided by API-Kolon.
Linear Mold Shrinkage	0.017 - 0.023 cm/cm	0.017 - 0.023 in/in	ASTM D1299
Loxim 200 00V0 Polybutylene Terephthalate Information provided by Loxim Industries
Linear Mold Shrinkage	0.017 - 0.023 cm/cm	0.017 - 0.023 in/in	ASTM D1299
Loxim 800 00 HB Polypropylene Compound, Flame Retardant Information provided by Loxim Industries
Linear Mold Shrinkage	<= 0.017 cm/cm	<= 0.017 in/in	Note 1
Monmouth Rubber & Plastics Durafoamâ„¢ P292HD EPDM Note 1: The Durafoamâ„¢100% EPDM Series, Expanded Cellular Rubber Sheets, were tested for QUV Ultraviolet Light Exposure. Test specimens for each stock number were cut 3 inches by 11 inches from ..
Linear Mold Shrinkage	<= 0.017 cm/cm	<= 0.017 in/in
Monmouth Rubber & Plastics Durafoamâ„¢ P97SHD Red EPDM The Durafoamâ„¢100% EPDM Series, Expanded Cellular Rubber Sheets, were tested for QUV Ultraviolet Light Exposure. Test specimens for each stock number were cut 3 inches by 11 inches from Â¼ inc..
Linear Mold Shrinkage	0.017 - 0.022 cm/cm	0.017 - 0.022 in/in
Lehmann & Voss LUVOCOMÂ® AC-80/TF/22/BK Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	0.125inch wall
Spartech PE4125 Reinforced High Density Polyethylene Compound Spartech Polycom's filled high molecular weight, high density polyethylenes are specifically designed for blow molding and sheet extrusion /thermoforming of structural parts. These materials offer a..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics ..
Linear Mold Shrinkage	0.017 - 0.025 cm/cm	0.017 - 0.025 in/in
Polyram PlusTek PA880 Nylon 6.6, Impact Modified Super tough - impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in
Tisan TISOPLEN® Flame Retardant (V0). Heat Stabilized, Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1008-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics ..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics ..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic..
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	Bayer Test
Covestro Bayflex® 180 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o..
Linear Mold Shrinkage	0.017 - 0.021 cm/cm	0.017 - 0.021 in/in	Asahi Kasei Method
Asahi Kasei Tenac® 7054 Homopolymer Acetal Resin High-flow grade with high crystallization rate for higher productivity.Information provided by Asahi Kasei Corporation.
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in	STN 64 0808
Plastcom SLOVALEN PH 51 T 20 Polypropylene Homopolymer, 20% Mineral Filled FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filler. Increased rigidity, strength and thermal use up to 130°C. Decreased shrinkage. General application ..
Linear Mold Shrinkage	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in	after bake; ISO 294
Solvay Engineered Polymers DEXPRO® R116 TPV - High-Impact Polypropylene (discontinued **) Description: DEXPRO® R116 is a thermoplastic polyolefin elastomeric. It is unfilled, reactor-grade molding compound. Applications: Exterior trim Information provided by Solvay Engineered Polymers..
Linear Mold Shrinkage	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in	ASTM D955
Samyang Triel® 5650 Thermoplastics Polyetherester Elastomer, General Extrusion Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5650 is an extrusion grade.Information provided by Samyang.