Polykemi AB POLYabs V0X ABS, Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | POLYabs |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYabs V0X ABS, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | With Flow; ISO 2577 |
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 18 g/10 min @Load 5.00 kg, Temperature 230 °C |
18 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 40.0 MPa | <= 5800 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 75.0 MPa | <= 10900 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -20.0 °C |
5.23 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 85.0 °C @Load 5.001 kg |
185 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 98.0 °C @Load 1.00 kg |
208 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 2.50 mm |
V-0 @Thickness 0.0984 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C @Thickness 2.50 mm |
1760 °F @Thickness 0.0984 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 210 °C | 374 - 410 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in fresh-air dryer | |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 1.00 - 1.50 MPa | 145 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | Medium |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 4070 Liquid Silicone Rubber - Healthcare
- SABIC Innovative Plastics ULTEM HU1004 PEI (Europe-Africa-Middle East)
- Teknor Apex APEX® 90-P513A-65-NT Polyvinyl Chloride+PUR
- Borealis Borstar® ME6052 Black Bimodal MD Polyethylene Compound for Jacketing of Communication and Power Cables
- Unifrax Fiberfrax® HS70C High Purity High-Index Fiber
- Westlake Plastics Radel® R Polyphenylsulfone
- BASF Polystyrol® 486 M Impact Grade Polystyrene (Europe)
- SABIC Innovative Plastics SABIC STAMAX 40YM243 PP
- HP Alloys Alloy 718, 50% Cold Worked, Aged
Copyright © lookpolymers.com All Rights Reserved