Lanxess Durethan® BG 30 X 000000 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BG 30 X 000000 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, low warpage
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 41 g/10 min @Load 5.00 kg, Temperature 260 °C |
41 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Conditioned; ISO 527-1/-2 |
| 125 MPa | 18100 psi | ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 10 % | 10 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | Conditioned; ISO 527-1/-2 |
| 6.40 GPa | 928 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Impact | 701 | 701 | Puncture maximum force (N); ISO 6603-2 |
| 686 @Temperature -30.0 °C |
686 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.00 J | 1.48 ft-lb | ISO 6603-2 |
| 1.70 J @Temperature -30.0 °C |
1.25 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 1.70 J @Temperature -30.0 °C |
1.25 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 2400 MPa | 348000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 2000 MPa | 290000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
IEC 60250 | |
| 4.8 @Frequency 1.00e+6 Hz |
4.8 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 16 @Frequency 100 Hz |
16 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; IEC 60243-1 |
| 36.0 kV/mm | 914 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.10 @Frequency 1.00e+6 Hz |
0.10 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.31 @Frequency 100 Hz |
0.31 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MR,14-060,(GB+GF)30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Homopolymer 134 HSL Nylon 6/6
- Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
- SABIC Innovative Plastics ULTEM 4001 PEI (Asia Pacific)
- Teknor Apex Telcar® TL-2478H Thermoplastic Elastomer
- Loctite® 3341 Light Cure Acrylic Adhesive
- CP-Polymer-Technik Wellamid® 6000 GVZ 45 HWCP 45% Glass Fiber Nylon 6, Impact Resistant, Good Surface Finish, Heat Stabilized, Dry
- China Tungsten YG22C Tungsten Carbide
- Bulk Molding Compounds BMC 1403 Electrical Grade
- Bulk Molding Compounds BMC T40(18)V0 Die Casting Replacement Grade Molding Compound
- Premix Premi-Glas® 1200-24 Polyester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved