Polykemi AB POLYabs SS0 GK10 ABS, High Flow
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Polykemi AB |
| Trade Name | POLYabs |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYabs SS0 GK10 ABS, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | With Flow; ISO 2577 |
| 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 30 g/10 min @Load 5.00 kg, Temperature 230 °C |
30 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 34.0 MPa | <= 4930 psi | ISO/R527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 67.0 MPa | <= 9720 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa @Temperature 23.0 °C |
305 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 98.0 °C @Load 5.001 kg |
208 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 105 °C @Load 1.00 kg |
221 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in fresh-air dryer | |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 1.00 - 1.50 MPa | 145 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- MV Labs K900 KH2PO4 Potassium dihydrogen phosphate
- Plaslok 308 Black (COM) Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
- Kotec Carbotex K-40MRA Polycarbonate, General Purpose, Mold Release Grade
- H.C. Starck Grade HP Boron Carbide, B4C
- SABIC Innovative Plastics LNP STAT-KON DX93500 PC
- Cytec EN-2523 (Conap) Potting and Encapsulation Adhesive
- AK Steel ASTM A 1011, Grade 50 Hot Rolled Carbon Steel, Structural Steel (SS)
- Bayshore Vinyl Compounds BVC 7200-65 Vinyl Compound
- ChevronTexaco Ulti-Plex® NLGI 2 Greases EP
Copyright © lookpolymers.com All Rights Reserved