- Acrylonitrile Butadiene Styrene (ABS), Molded
- Styrolution NOVODUR® P2H-AT ABS, Injection Grade
Styrolution NOVODUR® P2H-AT ABS, Injection Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution NOVODUR® P2H-AT ABS, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard injection molding grade, easy flow, high gloss, hard, antistatic.Applications: Telephones, household goods, video and audio industry, office equipment.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | Saturation in water |
| Water Absorption at Saturation | 0.30 % | 0.30 % | |
| Melt Flow | 37 g/10 min @Load 10.0 kg, Temperature 220 °C |
37 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | |
| Elongation at Yield | 2.1 % | 2.1 % | |
| Tensile Modulus | 2.60 GPa | 377 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | |
| Tensile Creep Modulus, 1000 hours | 1500 MPa | 218000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | |
| Vicat Softening Point | 95.0 °C | 203 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | |
| Dissipation Factor | 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
|
| 0.015 @Frequency 100 Hz |
0.015 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- MV Labs SN550 (NH4)2SnF6 Ammonium hexafluorostannate(IV)
- BASF Capron® GR20 20% Glass-Filled Nylon 6 (Dry) (discontinued **)
- A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene
- ELM® SoyFluid™ Hydraulic Industrial (ISO 46) Premium Biodegradable – Biobased Hydraulic Oil
- ExxonMobil Label-Lyte® 612 LLG-102 Clear OPP Film
- Fainplast Compounds PK 96 Flexible PVC, Lead Free
- 3M 80 Rubber and Vinyl Spray Adhesive
- BASF Heligoen® Green L 8605 Color Additive
Copyright © lookpolymers.com All Rights Reserved