Lanxess Durethan® AKV 35 HR H2.0 901510 Nylon 66, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 35 HR H2.0 901510 Nylon 66, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 35% glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ISO 1183
Moisture Absorption at Equilibrium 1.7 %
1.7 %
50% RH; ISO 62
Water Absorption at Saturation 5.2 %
5.2 %
ISO 62
Linear Mold Shrinkage, Flow 0.00060 cm/cm
0.00060 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0038 cm/cm
0.0038 in/in
60x60x2; 300°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.00090 cm/cm
0.00090 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0105 cm/cm
0.0105 in/in
60x60x2; 300°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
cond.; ISO 527-1, -2; 5 mm/min
195 MPa
28300 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.1 %
3.1 %
d.a.m.; ISO 527-1, -2; 5 mm/min
6.0 %
6.0 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 7.80 GPa
1130 ksi
cond.; ISO 527-1, -2; 1 mm/min
11.5 GPa
1670 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 210 MPa

@Strain 6.00 %
 30500 psi

@Strain 6.00 %
 cond., 2 mm/min; ISO 178-A
305 MPa

@Strain 3.80 %
 44200 psi

@Strain 3.80 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 180 MPa

@Strain 3.50 %
 26100 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
Flexural Modulus 7.00 GPa
1020 ksi
cond., 2 mm/min; ISO 178-A
10.7 GPa
1550 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 65.0 kJ/m²

@Temperature -30.0 °C
 30.9 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
75.0 kJ/m²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
Charpy Impact Unnotched 7.50 J/cm²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
8.50 J/cm²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
8.50 J/cm²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -40.0 °C
 <= 4.76 ft-lb/in²

@Temperature -40.0 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -40.0 °C
 <= 4.76 ft-lb/in²

@Temperature -40.0 °F
 cond.; ISO 179-1eA
1.30 J/cm²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 262 °C
504 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ISO 75-1, -2
Vicat Softening Point >= 230 °C

@Load 5.10 kg
 >= 446 °F

@Load 11.2 lb
 50°C/hour; ISO 306
255 °C

@Load 5.10 kg
 491 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Oxygen Index 26 %
26 %
Method A; ISO 4589-2
Glow Wire Test 650 °C

@Diameter 2.00 mm
 1200 °F

@Diameter 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
d.a.m.; IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
 3.6

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
3.9

@Frequency 100 Hz
 3.9

@Frequency 100 Hz
 d.a.m.; IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
 889 kV/in

@Thickness 0.0394 in
 d.a.m.; IEC 60243-1
Dissipation Factor 0.010

@Frequency 100 Hz
 0.010

@Frequency 100 Hz
 d.a.m.; IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
Comparative Tracking Index 425 V
425 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
290 °C
554 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Descriptive Properties Value Comments
Flammability Test passed
ISO 3795, = 1.0 mm
ISO Shortname ISO 1874-PA 66, GHRW, 14-110, GF30