- Lehmann & Voss LUVOCOM® 80-8510 Polyacetal-copolymer, with mineral filler, lubricant modified
Lehmann & Voss LUVOCOM® 80-8510 Polyacetal-copolymer, with mineral filler, lubricant modified
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Mineral Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-8510 Polyacetal-copolymer, with mineral filler, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.High dimensionally stable precision parts with low warpage and narrow tolerance range.Bearings, sleeves, sliding elements, handles, machine parts.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.010 - 0.017 cm/cm | 0.010 - 0.017 in/in | |
| Melt Flow | 9.66 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.66 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 55.0 MPa | 7980 psi | |
| Elongation at Yield | 4.5 % | 4.5 % | |
| 5.0 % | 5.0 % | flexural | |
| Modulus of Elasticity | 6.50 GPa | 943 ksi | |
| Flexural Strength | 95.0 MPa | 13800 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- Nye Lubricants 371B (RL) Synthetic Oil
- Paratherm Corporation Paratherm™ GLT™ Heat Transfer Fluid
- SABIC Innovative Plastics Lexan® HPH4704 PPC
- Mateck Gallium Arsenide (GaAs)
- Styron Magnumâ„¢ 2620 ABS, Impact Grade
- Dow Corning HIPEC® Q3-6645 SEMICONDUCTOR PROTECTIVE COATING KIT
- Braskem PB 682 LDPE Blow Molding Polyethylene
- Arlon 56976XA026 Silicone Rubber/Fiberglass Laminate
- BASF Ultraform® N2650 Z6 POM + PUR
- BP Amoco Accpro® 9346 Enhanced Polypropylene (discontinued **)