LG Chemical Lupox® TE5006F PET+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer LG Chemical
Trade Name Lupox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® TE5006F PET+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PET+PC, Flame Retardant, GWIT, CTIApplication: IT/OA, E&E (Connector)CAS No. 68928-70-1, 103598-77-2, 25038-59-9 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.010 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.8 MPa

@Thickness 3.20 mm
 8530 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 100 %

@Thickness 3.20 mm
 >= 100 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 88.3 MPa

@Thickness 3.20 mm
 12800 psi

@Thickness 0.126 in
 2.8mm/min; ASTM D790
Flexural Modulus 2.30 GPa

@Thickness 3.20 mm
 334 ksi

@Thickness 0.126 in
 2.8mm/min; ASTM D790
Izod Impact, Notched 0.588 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.10 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 6.40 mm
 230 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 75.0 °C

@Thickness >=0.500 mm
 167 °F

@Thickness >=0.0197 in
110 °C

@Thickness >=0.750 mm
 230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.00 mm
 230 °F

@Thickness >=0.0394 in
120 °C

@Thickness >=1.60 mm
 248 °F

@Thickness >=0.0630 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 75.0 °C

@Thickness >=0.500 mm
 167 °F

@Thickness >=0.0197 in
110 °C

@Thickness >=0.750 mm
 230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.00 mm
 230 °F

@Thickness >=0.0394 in
120 °C

@Thickness >=1.60 mm
 248 °F

@Thickness >=0.0630 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 75.0 °C

@Thickness >=0.500 mm
 167 °F

@Thickness >=0.0197 in
110 °C

@Thickness >=0.750 mm
 230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.00 mm
 230 °F

@Thickness >=0.0394 in
120 °C

@Thickness >=1.60 mm
 248 °F

@Thickness >=0.0630 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=0.500 mm
 V-0

@Thickness >=0.0197 in
V-0

@Thickness >=0.750 mm
 V-0

@Thickness >=0.0295 in
V-0

@Thickness >=1.00 mm
 V-0

@Thickness >=0.0394 in
V-0

@Thickness >=1.60 mm
 V-0

@Thickness >=0.0630 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
5VB

@Thickness >=1.60 mm
 5VB

@Thickness >=0.0630 in
5VA

@Thickness >=3.00 mm
 5VA

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness >=0.750 mm
 30 - 60 sec

@Thickness >=0.0295 in
30 - 60 sec

@Thickness >=1.00 mm
 30 - 60 sec

@Thickness >=0.0394 in
30 - 60 sec

@Thickness >=1.60 mm
 30 - 60 sec

@Thickness >=0.0630 in
60 - 120 sec

@Thickness >=3.00 mm
 60 - 120 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
>= 120 arcs

@Thickness 1.00 mm
 >= 120 arcs

@Thickness 0.0394 in
>= 120 arcs

@Thickness 1.60 mm
 >= 120 arcs

@Thickness 0.0630 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Injection Molding
Middle Barrel Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Front Barrel Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Nozzle Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Melt Temperature 260 - 270 °C
500 - 518 °F
Injection Molding
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding