LG Chemical LUPOY SR3108L PC, High Impact

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY SR3108L PC, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC, High Flow, High Impact, White Color OnlyApplication: BLU Mold frame for Mobile DevicesCAS: 103598-77-2 and 13463-67-1Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0080 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 25 g/10 min
<br>@Load 1.20 kg,<br> Temperature 300 °C
 25 g/10 min
<br>@Load 2.65 lb,<br> Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D785
Tensile Strength, Yield 53.9 MPa
<br>@Thickness 3.20 mm
 7820 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 100 %
<br>@Thickness 3.20 mm
 100 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 88.3 MPa
<br>@Thickness 3.20 mm
 12800 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.26 GPa
<br>@Thickness 3.20 mm
 327 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 5.88 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 >= 11.0 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 124 °C
<br>@Thickness 6.40 mm
 255 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C
176 °F
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL RTI, Mechanical without Impact 80.0 °C
176 °F
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Injection Molding
Middle Barrel Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Nozzle Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Melt Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding