LG Chemical LUPOY GN5001RFM PC/ABS, Halogen Free Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN5001RFM PC/ABS, Halogen Free Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, General PurposeApplication: E&E (Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 9.5 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 9.5 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 54.9 MPa

@Thickness 3.20 mm
 7970 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 50 %

@Thickness 3.20 mm
 >= 50 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 86.3 MPa

@Thickness 3.20 mm
 12500 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 3.20 mm
 341 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched 4.90 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 9.18 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C

@Thickness 6.40 mm
 198 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.20 mm
 140 °F

@Thickness >=0.0472 in
80.0 °C

@Thickness >=1.50 mm
 176 °F

@Thickness >=0.0591 in
80.0 °C

@Thickness >=2.00 mm
 176 °F

@Thickness >=0.0787 in
80.0 °C

@Thickness >=2.50 mm
 176 °F

@Thickness >=0.0984 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.20 mm
 140 °F

@Thickness >=0.0472 in
80.0 °C

@Thickness >=1.50 mm
 176 °F

@Thickness >=0.0591 in
80.0 °C

@Thickness >=2.00 mm
 176 °F

@Thickness >=0.0787 in
80.0 °C

@Thickness >=2.50 mm
 176 °F

@Thickness >=0.0984 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.20 mm
 140 °F

@Thickness >=0.0472 in
85.0 °C

@Thickness >=1.50 mm
 185 °F

@Thickness >=0.0591 in
85.0 °C

@Thickness >=2.00 mm
 185 °F

@Thickness >=0.0787 in
85.0 °C

@Thickness >=2.50 mm
 185 °F

@Thickness >=0.0984 in
85.0 °C

@Thickness >=3.00 mm
 185 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.20 mm
 V-0

@Thickness >=0.0472 in
V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.00 mm
 V-0

@Thickness >=0.0787 in
V-0

@Thickness >=2.50 mm
 V-0

@Thickness >=0.0984 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
5VB

@Thickness >=2.50 mm
 5VB

@Thickness >=0.0984 in
5VB

@Thickness >=3.00 mm
 5VB

@Thickness >=0.118 in
5VA

@Thickness >=1.50 mm
 5VA

@Thickness >=0.0591 in
5VA

@Thickness >=2.00 mm
 5VA

@Thickness >=0.0787 in
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness >=1.20 mm
 30 - 60 sec

@Thickness >=0.0472 in
30 - 60 sec

@Thickness >=1.50 mm
 30 - 60 sec

@Thickness >=0.0591 in
30 - 60 sec

@Thickness >=2.00 mm
 30 - 60 sec

@Thickness >=0.0787 in
High Amp Arc Ignition, HAI 30 - 60 arcs

@Thickness 1.20 mm
 30 - 60 arcs

@Thickness 0.0472 in
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 2.00 mm
 >= 120 arcs

@Thickness 0.0787 in
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 260 °C
446 - 500 °F
Injection Molding
Middle Barrel Temperature 230 - 260 °C
446 - 500 °F
Injection Molding
Front Barrel Temperature 230 - 260 °C
446 - 500 °F
Injection Molding
Nozzle Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Melt Temperature 230 - 260 °C
446 - 500 °F
Injection Molding
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Injection Molding
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding