- LG Chemical LUPOY EC5000AF PC/ABS, Flame Residence
LG Chemical LUPOY EC5000AF PC/ABS, Flame Residence
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY EC5000AF PC/ABS, Flame Residence.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Flame Residence, Anti-StaticApplication: E&E (Housing)CAS: 103598-77-2, 9003-56-9 and 68928-70-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 250 °C |
11 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 50 % @Thickness 3.20 mm |
>= 50 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 85.3 MPa @Thickness 3.20 mm |
12400 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa @Thickness 3.20 mm |
356 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 9.18 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.60 - 1.70 mm |
140 °F @Thickness 0.0630 - 0.0669 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.60 - 1.70 mm |
140 °F @Thickness 0.0630 - 0.0669 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.60 - 1.70 mm |
140 °F @Thickness 0.0630 - 0.0669 in |
|
| Flammability, UL94 | V-2 @Thickness 1.60 - 1.70 mm |
V-2 @Thickness 0.0630 - 0.0669 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 215 - 250 °C | 419 - 482 °F | Injection Molding |
| Front Barrel Temperature | 225 - 260 °C | 437 - 500 °F | Injection Molding |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Northstar Polymers MPC-023 Isocyanate Prepolymer
- Polyram BondyRam® 2001 Maleic Anhydride modified EVA coupling agent (discontinued **)
- IRPC Polimaxx Polene 2346S Polypropylene Block Copolymer
- SABIC Innovative Plastics LNP Thermocomp GF008 PSU (Asia Pacific)
- Silberline Silvex® 223-20-C
- Unifrax IsoMat® AV/AVi Substrate Support Mat
- Tipco Tipcofil® AG 600 - 30% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
- AK Steel SAE J1392 050 XLK, Grade 50 Aluminized Carbon Steel, High Strength Low Alloy Steel (HSLAS)
- PolyOne Synprene® RT-3630 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved