PolyOne Geon™ Vinyl Rigid Extrusion 87358 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87358 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 46.5 MPa | 6740 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.56 GPa | 371 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 78.6 MPa | 11400 psi | ASTM D790 |
| Flexural Modulus | 2.74 GPa | 397 ksi | ASTM D790 |
| Izod Impact, Notched | 3.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
6.18 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 4.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
7.87 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| 5.80 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
10.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 63.2 J/cm @Temperature 23.0 °C |
0.118 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 199 J/cm @Temperature 23.0 °C |
0.373 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C | 41.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.6 °C @Thickness 3.18 mm |
141 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 193 °C | 370 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | High Gloss | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Sheet Extrusion | |
| Thermoforming | ||
| PVC Cell Classification | 15343 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Dielectric Polymers NT-500 Protective Film (discontinued **)
- Global PP-2340-TC Polypropylene Block Copolymer
- LG Chemical AF305HT ABS, Flame Retardant, Heat Resistance
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 55-LR-9 TPE
- Saint-Gobain CHR® 2253-2 High Modulus PTFE Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Wingate Alloys Winco HCP 60 Induction Hardened Turned, Ground and Polished, Hard Chromium Plated Shafting
- Clariant Renol BR7140 Polycarbonate/ABS Alloy
- Compuestos Dominicanos Polycom VY-050775 PVC Compound
- Resistalloy International Resistalloy 6015 Nickel Chromium Electrical Resistance Alloy
- Beijing Ranger Chem SM-602R Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved