LATI Larton G/40 I6 PPS, 40% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer LATI
Trade Name Larton
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton G/40 I6 PPS, 40% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Glass fibers. Good elongation. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0045 cm/cm
0.0015 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.011 cm/cm
0.0070 - 0.011 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa

@Temperature 150 °C
 12300 psi

@Temperature 302 °F
110 MPa

@Temperature 120 °C
 16000 psi

@Temperature 248 °F
150 MPa

@Temperature 90.0 °C
 21800 psi

@Temperature 194 °F
180 MPa

@Temperature 60.0 °C
 26100 psi

@Temperature 140 °F
195 MPa

@Temperature 23.0 °C
 28300 psi

@Temperature 73.4 °F
Elongation at Break 1.7 %

@Temperature 23.0 °C
 1.7 %

@Temperature 73.4 °F
1.7 %

@Temperature 60.0 °C
 1.7 %

@Temperature 140 °F
2.6 %

@Temperature 90.0 °C
 2.6 %

@Temperature 194 °F
3.0 %

@Temperature 120 °C
 3.0 %

@Temperature 248 °F
3.3 %

@Temperature 150 °C
 3.3 %

@Temperature 302 °F
Tensile Modulus 6.00 GPa

@Temperature 150 °C
 870 ksi

@Temperature 302 °F
9.20 GPa

@Temperature 120 °C
 1330 ksi

@Temperature 248 °F
14.0 GPa

@Temperature 90.0 °C
 2030 ksi

@Temperature 194 °F
14.5 GPa

@Temperature 60.0 °C
 2100 ksi

@Temperature 140 °F
15.0 GPa

@Temperature 23.0 °C
 2180 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 44 %
44 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 125 V
125 V
A solution
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa