LG Chemical LUMID GP2130B(W) PA66+GF13%, General Purpose

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GP2130B(W) PA66+GF13%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA66+GF13%, General PurposeApplication: Valve CoversCAS No. 32131-17-2, 65997-17-3 and 9010-79-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Water Absorption 1.0 %

@Temperature 23.0 °C,
Time 86400 sec
 1.0 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Maximum Moisture Content 0.090
0.090
Injection Molding
Linear Mold Shrinkage, Flow 0.0070 - 0.012 cm/cm

@Thickness 3.20 mm
 0.0070 - 0.012 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Yield 123 MPa

@Thickness 3.20 mm
 17800 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 4.0 %

@Thickness 3.20 mm
 4.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 167 MPa

@Thickness 3.20 mm
 24200 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 4.90 GPa

@Thickness 3.20 mm
 711 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 0.918 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 255 °C

@Thickness 6.40 mm
 491 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 240 °C

@Thickness 6.40 mm
 464 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 120 °C

@Thickness >=0.750 mm
 248 °F

@Thickness >=0.0295 in
120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 110 °C

@Thickness >=0.750 mm
 230 °F

@Thickness >=0.0295 in
110 °C

@Thickness >=1.50 mm
 230 °F

@Thickness >=0.0591 in
110 °C

@Thickness >=3.00 mm
 230 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 120 °C

@Thickness >=0.750 mm
 248 °F

@Thickness >=0.0295 in
120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=0.700 mm
 HB

@Thickness >=0.0276 in
HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 25.0 kV/mm

@Thickness 1.00 mm
 635 kV/in

@Thickness 0.0394 in
 ASTM D149
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=0.700 mm
 15 - 30 sec

@Thickness >=0.0276 in
15 - 30 sec

@Thickness >=1.50 mm
 15 - 30 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.700 mm
 >= 120 arcs

@Thickness 0.0276 in
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 275 - 285 °C
527 - 545 °F
Injection Molding
Middle Barrel Temperature 270 - 280 °C
518 - 536 °F
Injection Molding
Front Barrel Temperature 270 - 285 °C
518 - 545 °F
Injection Molding
Nozzle Temperature 270 - 280 °C
518 - 536 °F
Injection Molding
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection Molding
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding