A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Outokumpu 4878 High Temperature Austenitic Stainless Steel
- SABIC Innovative Plastics LNP LUBRICOMP DL0039E PC (Europe-Africa-Middle East)
- Resinoid 1370 Phenolic Molding, Glass Reinforced
- MarkeTech Yttrium Aluminate (YAlO3) Single Crystal Substrate
- Lubrizol ESTANE® 58630 Ether Based Thermoplastic Polyurethane (European Grade)
- Asahi Kasei Tenac® SH710 Homopolymer Acetal Resin
- Von Roll Isola IMI Varnish 707 Solventless Polyester Varnish for Electrical Insulation
- Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved