LG Chemical LUMID GN1001BF PA66, Halogen Free Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer LG Chemical
Trade Name LUMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GN1001BF PA66, Halogen Free Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA66, Halogen Free Flame RetardantApplication: ConnectorsCAS No. 32131-17-2, 25038-54-4 and 37640-57-6Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Water Absorption 1.3 %

@Temperature 23.0 °C,
Time 86400 sec
 1.3 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Maximum Moisture Content 0.10
0.10
Injection Molding
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 3.20 mm
 0.0090 - 0.016 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 78.5 MPa

@Thickness 3.20 mm
 11400 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
 30 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 113 MPa

@Thickness 6.40 mm
 16400 psi

@Thickness 0.252 in
 2.8mm/min; ASTM D790
Flexural Modulus 3.04 GPa

@Thickness 6.40 mm
 441 ksi

@Thickness 0.252 in
 2.8mm/min; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 0.918 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ASTM D696
Melting Point 260 °C
500 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 240 °C

@Thickness 6.40 mm
 464 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 6.40 mm
 185 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 0.750 - 0.820 mm
 149 °F

@Thickness 0.0295 - 0.0323 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 - 0.820 mm
 149 °F

@Thickness 0.0295 - 0.0323 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 - 0.820 mm
 149 °F

@Thickness 0.0295 - 0.0323 in
Flammability, UL94 V-0

@Thickness >=0.800 mm
 V-0

@Thickness >=0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 22.0 kV/mm

@Thickness 1.00 mm
 559 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 180 - 240 sec
180 - 240 sec
ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 0.750 - 0.820 mm
 15 - 30 sec

@Thickness 0.0295 - 0.0323 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 255 - 280 °C
491 - 536 °F
Injection Molding
Middle Barrel Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Front Barrel Temperature 260 - 275 °C
500 - 527 °F
Injection Molding
Nozzle Temperature 270 - 280 °C
518 - 536 °F
Injection Molding
Melt Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding