Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: machine parts under 80 mm diameter, hammer-heads, cup-shaped bearing shellsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 2.5 - 3.0 % | 2.5 - 3.0 % | DIN 53473 |
| Water Absorption at Saturation | 8.5 - 10 % @Temperature 20.0 °C |
8.5 - 10 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ISO-DIS 527 |
| Creep Strength | >= 7.00 MPa | >= 1020 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 10.5 MPa | >= 1520 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 1.80 GPa | 261 ksi | DIN 53457 |
| Flexural Strength | 40.0 MPa | 5800 psi | DIN 54352 |
| Flexural Modulus | 1.40 GPa | 203 ksi | DIN 53457 |
| Izod Impact, Notched (ISO) | NB | NB | DIN 53453 |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.080 | 0.080 | With lubrication |
| Coefficient of Friction, Dynamic | 0.42 | 0.42 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 1.6 | >= 1.6 | ISO-DIS 527 |
| K Factor (Wear Factor) | 2.3e-10 | 2.3e-10 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 100 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 55.6 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous |
| 160 °C | 320 °F | Intermittent | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | DIN 53482 |
| Dielectric Constant | 7.0 | 7.0 | DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.30 | 0.30 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3b | DIN 53480 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRESEAL® TPE 6070
- Karina E 90/212-DA-IS-SI-AT Compound PVC Crystal
- Industeel CLC 18.10 Nb Niobium Stabilized 18Cr-10Ni Austenitic Stainless Steel
- H.C. Starck Amperit® 554.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- Mearthane Durethaneâ„¢ S DS-665D Solid Polyurethane Elastomer
- SABIC Innovative Plastics Valox® VC130 PBT (Asia Pacific)
- A. Schulman POLYBATCH™ Deep Red 50389 Concentrate Based In Linear Low-Density Polyethylene
- A. Schulman POLYBLAK™ 4692 Premium Black Color Concentrate, 35% Carbon Black Based In LLDPE
- 3M Scotch-Weld™ 1838 B/A Tan Two-Part Structural Adhesive
- Ashley Polymers Ashlene® 830LB Nylon 6
Copyright © lookpolymers.com All Rights Reserved