Kingfa JE2-R2 ABS/PBT Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa JE2-R2 ABS/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Low costExcellent balance propertiesGood processing propertiesGood heat stabilityGood size stabilityGood surfaceApplications:CD-ROM, DVDPrinter, scanner, photocopier cabinetElectric and electronic partsAutomobile partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc @Temperature 23.0 °C |
1.07 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Temperature 23.0 °C |
0.0060 - 0.0080 in/in @Temperature 73.4 °F |
Plumb; ASTM D955 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0060 in/in @Temperature 73.4 °F |
ASTM D955 |
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 230 °C |
22 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50mm/min; ASTM D638 |
| Elongation at Break | >= 20 % | >= 20 % | 50mm/min; ASTM D638 |
| Flexural Strength | 65.0 MPa | 9430 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 2.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
3.93 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 250 °C | <= 482 °F | |
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Start Point: 215°C |
| Middle Barrel Temperature | 220 - 230 °C | 428 - 446 °F | Start Point: 225°C |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 - 14400 sec |
176 - 194 °F @Time 3.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | 60-80% |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® BX9349 PC COPOLYMER (Asia Pacific)
- Honeywell Aegis™ HCA73ZP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- Multibase Multi-Flex® G 7890 TPE Styrene Ethylene Butylene Styrene Block Copolymer
- Lehmann & Voss LUVOCOM® 1-0866 Polyamide 66, with aramid reinforcement, heat stabilized
- Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Rod and Bar
- Chengdu Polyster FH7560 Thermoplastic Polyether-ester Elastomer (TPEE)
- China Tungsten STG60-25 PM Structural Parts
- China Tungsten YG20 Tungsten Carbide for Dies and Wear Part Making
- Biomer P240 PHB Biodegradable Polymer
Copyright © lookpolymers.com All Rights Reserved