Clariant PA131G2GN-91 Green Nylon 66, Highly Toughened
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant PA131G2GN-91 Green Nylon 66, Highly Toughened.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Flexural Yield Strength | 66.2 MPa | 9600 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 7.74 J/cm @Temperature 22.8 °C |
14.5 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 113 Ground Alumina
- Polimeri Europa Intex® 131 Styrene - Butadiene Copolymer
- MV Labs ZN1000 ZnSO4·7H2O Zinc sulfate heptahydrate
- Fibre Glast 3100 Style 7781 Prepreg E-Glass Fiberglass Fabric
- Mar-Bal MB2000-5 Thermoset Polyester Composite Molding Compound
- Arlon 28601M015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Arlon T3030-R004 0.030" (0.762 mm) Thick, 1" wide, Cured Fusible Silicone Rubber with Sinusoidal Fiberglass Substrate
- Arkema Group Orgalloy® R 6030 Nylon 6 Alloy, 30% Glass fiber (Conditioned)
Copyright © lookpolymers.com All Rights Reserved