Samsung Cheil Industries Infino® GW-1010 PC, Unreinforced Recycled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GW-1010 PC, Unreinforced Recycled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 250 °C |
18 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 78.5 MPa | 11400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.01 GPa | 292 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 7.85 J/cm @Thickness 3.17 mm |
14.7 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 140 °C | 284 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
Users viewing this material also viewed the following:
- Nylene® Vexel™ B50U , High Flow, Un-reinforced PBT
- Polimeri Europa Riblene® FH 10 Low Density Polyethylene - Blown Film Extrusion
- LG Chemical Lupoy 3030-10 Polycarbonate Resin
- Karina E 813-10/164-B-RT-PO White PVC Compound
- SABIC Innovative Plastics Valox® 325 PBT (Europe-Africa-Middle East)
- Sinotek Materials ZSLZ92 Middle Carbon Graphite
- Hexcel® HexForce™ AGP370-5H Carbon Fabric
- CMW® D54X Post-oxidized Silver Cadmium Oxide Contact Material ASTM B781, Table 3
- Asahi Glass Fluon® L169J PTFE Lubricant
- Asahi Kasei Xyron® 500H Modified Polyphenylene Ether
Copyright © lookpolymers.com All Rights Reserved