Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® M344 BLK is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016”) thick.Availability:Asia PacificEuropeNorth America Additive:HalogenLubricant Features:DuctileFlame RetardantGood Crack ResistanceGood Mold ReleaseGood ToughnessHalogenatedHigh ElongationIgnition ResistantLow DensityLubricatedUses:AppliancesAutomotive ElectronicsBobbinsConnectorsElectrical HousingElectrical PartsElectrical/Electronic ApplicationsFastenersIndustrial ApplicationsLighting ApplicationsLiving HingesPrinted Circuit BoardsSwitchesAppearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Water Absorption 0.80 %

@Time 86400 sec
 0.80 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 1.9 %
1.9 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.013 cm/cm

@Diameter 2.00 mm
 0.013 in/in

@Diameter 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Diameter 2.00 mm
 0.018 in/in

@Diameter 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-2
Elongation at Break 35 %
35 %
ISO 527-2
Elongation at Yield 5.2 %
5.2 %
ISO 527-2
Tensile Modulus 3.50 GPa
508 ksi
ISO 527-2
Flexural Strength 90.0 MPa
13100 psi
ISO 178
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.520 J/cm²

@Temperature -30.0 °C
 2.47 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.550 J/cm²

@Temperature 23.0 °C
 2.62 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 250 °C
482 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 186 °C
367 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746
130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746
65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
 UL 746
95.0 °C

@Thickness 1.50 mm
 203 °F

@Thickness 0.0591 in
 UL 746
95.0 °C

@Thickness 3.00 mm
 203 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 UL 746
95.0 °C

@Thickness 0.750 mm
 203 °F

@Thickness 0.0295 in
 UL 746
95.0 °C

@Thickness 1.50 mm
 203 °F

@Thickness 0.0591 in
 UL 746
95.0 °C

@Thickness 3.00 mm
 203 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Oxygen Index 30 %
30 %
ISO 4589-2
Glow Wire Test 700 °C

@Thickness 0.750 mm
 1290 °F

@Thickness 0.0295 in
 Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 Ignition Temperature; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
 1340 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
 1760 °F

@Thickness 0.0295 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm

@Thickness 0.750 mm
 1.00e+10 ohm-cm

@Thickness 0.0295 in
 IEC 60093
Dielectric Strength 26.0 kV/mm

@Thickness 1.00 mm
 660 kV/in

@Thickness 0.0394 in
 IEC 60243
Arc Resistance 60 - 119 sec

@Thickness 3.00 mm
 60 - 119 sec

@Thickness 0.118 in
 ASTM D495
Comparative Tracking Index 400 - 599 V

@Thickness 3.00 mm
 400 - 599 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.750 mm
 >= 120 sec

@Thickness 0.0295 in
 UL 746
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 UL 746
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 10.1 - 25.4 mm/min
0.398 - 1.00 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Middle Barrel Temperature 240 - 270 °C
464 - 518 °F
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Nozzle Temperature 240 - 270 °C
464 - 518 °F
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %