- Polymer Property : Tensile Strength at Break = 110 MPa
Polymer Property : Tensile Strength at Break = 110 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa @Temperature 175 °C |
16000 psi @Temperature 347 °F |
ISO 527 |
| Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 30% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food cont.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 175 °C |
16000 psi @Temperature 347 °F |
ISO 527 |
| Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact com.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® FE270038 BK267 Nylon 66
(Unverified Data**) Zytel® FE270038 is a 40% glass fiber/mineral reinforced, heat stabilized polyamid 66 for injection molding. It is well suited for water injection technology.Information provided by DuPont Performan.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® 73G30HSL BK261 Nylon 6
(Unverified Data**) Zytel® 73G30HSL BK261 is a 30% glass fiber reinforced, heat stabilized, lubricated, black polyamide 6 for injection molding. It has excellent surface appearance and gloss.Information provided by Du.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® 73G30T NC010 Nylon 6
(Unverified Data**) Zytel® 73G30T NC010 is a 30% glass fiber reinforced, toughened polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Laramid G/30-V0HF1 PPA, 30% Glass Fiber Reinforced, Flame Retardant Semi-aromatic polyamide (PPA) based compound. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good thermal properties. Good chemical resistance. Low.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 150 °C |
16000 psi @Temperature 302 °F |
|
| LATI Larpeek 50 G/30 PEEK, 30% Glass Fiber Reinforced Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Latamid 12 G/50 PA 12, 50% Glass Fiber Reinforced Polyamide 12 (PA12) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Latamid 66 E21 K/30 PA 66, 30% Carbon Fiber Reinforced Polyamide 66 (PA66) based compound. Toughened. Carbon fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastic.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Latamid 66 H2 G/35-V0KB PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Latamid 66 H2 G/35-V0KB3 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Latamid 66 H2 G/50-GWHF1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. improved G.W.F.I. compared to standard product.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ameri.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
|
| LATI Latamid 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Latamid 66 LH2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Oil stabilized. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Lapex A G/20 PES, 20% Glass Fiber Reinforced Polyether Sulfone (PES) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin Americ.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
|
| LATI Lapex R G/20 PPSU, 20% Glass Reinforced Polyphenylene Sulfone (PPSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin A.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
|
| LATI Laramid G/15 PPA, 15% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Larpeek 10 G/15 PEEK, 15% Glass Fiber Reinforced Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 150 °C |
16000 psi @Temperature 302 °F |
|
| LATI Larpeek 10 K/40 HM PEEK, 40% Carbon Fiber Reinforced Polyetheretherketone (PEEK) based compound. Carbon fiber. High tensile modulus. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Af.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
|
| LATI Larton G/40 I6 PPS, 40% Glass Fiber Reinforced Polyphenylene Sulfide (PPS) based compound. Glass fibers. Good elongation. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa .. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Lasulf G/30 PSU, 30% Glass Fiber Reinforced Polysulfone (PSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stabilityAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; Nort.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Latamid 66 H2 G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termop.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplasti.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
|
| LATI Latigloss 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized Product with high mechanical properties and exceptional surface finish based on Polyamide 66 (PA66). Heat stabilized. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin A.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
|
| LATI Latilon 28D K/20 PC, 20% Carbon Fiber Reinforced Polycarbonate (PC) based compound. Carbon fiber. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided b.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Minlon® FE6190 BK086 Nylon 66 Minlon® FE6190 BK086 is a 36% mineral/glass reinforced, heat stabilized, black polyamide resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® FR70G25V0 NC010 Nylon 66
(Unverified Data**) Zytel® FR70G25V0 NC010 is a 25% glass fiber reinforced, heat stabilized, flame retardant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
ISO 527 |
| DuPont Performance Polymers Crastin® HR5315HF NC010 PBT
(Unverified Data**) Crastin® HR5315HF is a 15% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resis.. |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Zytel® BM70G15HSLR BK537 Nylon 66 Zytel® BM70G15HSLR BK537 is a 15% glass fiber reinforced polyamide 66 for blow molding.Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
|
| LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn.. |
|||