DuPont Performance Polymers Zytel® FE270038 BK267 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® FE270038 BK267 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® FE270038 is a 40% glass fiber/mineral reinforced, heat stabilized polyamid 66 for injection molding. It is well suited for water injection technology.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
DAM; ISO 1183
Water Absorption 1.5 %

@Thickness 1.00 mm,
Temperature 23.0 °C
1.5 %

@Thickness 0.0394 in,
Temperature 73.4 °F
Equilibrium 50%RH; DAM; ISO 62, Similar to
5.0 %

@Thickness 1.00 mm,
Temperature 23.0 °C
5.0 %

@Thickness 0.0394 in,
Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
0.0030 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 2.00 mm
0.0070 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa

@Temperature 23.0 °C
16000 psi

@Temperature 73.4 °F
50%RH; ISO 527
145 MPa

@Temperature 23.0 °C
21000 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 2.5 %

@Temperature 23.0 °C
2.5 %

@Temperature 73.4 °F
DAM; ISO 527
2.6 %

@Temperature 23.0 °C
2.6 %

@Temperature 73.4 °F
50%RH; ISO 527
Tensile Modulus 7.80 GPa

@Temperature 23.0 °C
1130 ksi

@Temperature 73.4 °F
50%RH; ISO 527
8.80 GPa

@Temperature 23.0 °C
1280 ksi

@Temperature 73.4 °F
DAM; ISO 527
Charpy Impact Unnotched 4.10 J/cm²

@Temperature 23.0 °C
19.5 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eU
4.10 J/cm²

@Temperature 23.0 °C
19.5 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
33.3 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
Melting Point 245 °C
473 °F
10°C/min; DAM; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
DAM; ISO 75-1/-2
Glass Transition Temp, Tg 90.0 °C
194 °F
10°C/min; DAM; ISO 11357-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+12 ohm-cm

@Temperature 23.0 °C
2.00e+12 ohm-cm

@Temperature 73.4 °F
50%RH; IEC 60093
8.00e+14 ohm-cm

@Temperature 23.0 °C
8.00e+14 ohm-cm

@Temperature 73.4 °F
DAM; IEC 60093
Surface Resistance 3.00e+14 ohm

@Temperature 23.0 °C
3.00e+14 ohm

@Temperature 73.4 °F
50%RH; IEC 60093
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
DAM
290 °C
554 °F
DAM; Optimum
Mold Temperature 70.0 - 120 °C
158 - 248 °F
DAM
100 °C
212 °F
DAM; optimum
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Forms Pellets
DAM
Material Status Preliminary Data
DAM
Processing Method Injection Molding
DAM
Product Category Glass Reinforced Resins
DAM
Glass/Mineral Reinforced Resins
DAM
RoHS Compliance Contact Manufacturer
DAM