LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0105 - 0.013 cm/cm
0.0105 - 0.013 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa

@Temperature 150 °C
 5080 psi

@Temperature 302 °F
40.0 MPa

@Temperature 120 °C
 5800 psi

@Temperature 248 °F
50.0 MPa

@Temperature 90.0 °C
 7250 psi

@Temperature 194 °F
70.0 MPa

@Temperature 60.0 °C
 10200 psi

@Temperature 140 °F
110 MPa

@Temperature 23.0 °C
 16000 psi

@Temperature 73.4 °F
Elongation at Break 2.2 %

@Temperature 23.0 °C
 2.2 %

@Temperature 73.4 °F
4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
5.0 %

@Temperature 150 °C
 5.0 %

@Temperature 302 °F
5.5 %

@Temperature 120 °C
 5.5 %

@Temperature 248 °F
6.0 %

@Temperature 90.0 °C
 6.0 %

@Temperature 194 °F
Elongation at Yield 3.5 %

@Temperature 60.0 °C
 3.5 %

@Temperature 140 °F
4.8 %

@Temperature 150 °C
 4.8 %

@Temperature 302 °F
5.0 %

@Temperature 120 °C
 5.0 %

@Temperature 248 °F
5.2 %

@Temperature 90.0 °C
 5.2 %

@Temperature 194 °F
Tensile Modulus 2.00 GPa

@Temperature 150 °C
 290 ksi

@Temperature 302 °F
2.30 GPa

@Temperature 120 °C
 334 ksi

@Temperature 248 °F
2.80 GPa

@Temperature 90.0 °C
 406 ksi

@Temperature 194 °F
4.70 GPa

@Temperature 60.0 °C
 682 ksi

@Temperature 140 °F
6.80 GPa

@Temperature 23.0 °C
 986 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²

@Temperature -20.0 °C
 23.8 ft-lb/in²

@Temperature -4.00 °F
6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
 3.81 ft-lb/in²

@Temperature -4.00 °F
1.30 J/cm²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
Vicat Softening Point 235 °C

@Load 5.00 kg
 455 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 27 %
27 %
Glow Wire Test 775 °C

@Thickness 1.00 mm
 1430 °F

@Thickness 0.0394 in
 GWIT
800 °C

@Thickness 2.00 mm
 1470 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: