LATI Larpeek 50 G/30 PEEK, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer LATI
Trade Name Larpeek
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larpeek 50 G/30 PEEK, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0050 cm/cm
0.0025 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa

@Temperature 150 °C
 16000 psi

@Temperature 302 °F
135 MPa

@Temperature 120 °C
 19600 psi

@Temperature 248 °F
155 MPa

@Temperature 90.0 °C
 22500 psi

@Temperature 194 °F
160 MPa

@Temperature 60.0 °C
 23200 psi

@Temperature 140 °F
175 MPa

@Temperature 23.0 °C
 25400 psi

@Temperature 73.4 °F
Elongation at Break 2.2 %

@Temperature 23.0 °C
 2.2 %

@Temperature 73.4 °F
2.2 %

@Temperature 60.0 °C
 2.2 %

@Temperature 140 °F
2.2 %

@Temperature 90.0 °C
 2.2 %

@Temperature 194 °F
2.4 %

@Temperature 150 °C
 2.4 %

@Temperature 302 °F
23 %

@Temperature 120 °C
 23 %

@Temperature 248 °F
Tensile Modulus 10.4 GPa

@Temperature 150 °C
 1510 ksi

@Temperature 302 °F
10.6 GPa

@Temperature 120 °C
 1540 ksi

@Temperature 248 °F
11.0 GPa

@Temperature 90.0 °C
 1600 ksi

@Temperature 194 °F
11.3 GPa

@Temperature 60.0 °C
 1640 ksi

@Temperature 140 °F
11.5 GPa

@Temperature 23.0 °C
 1670 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 230 °C
446 °F
Deflection Temperature at 0.46 MPa (66 psi) >= 300 °C
>= 572 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 300 °C
>= 572 °F
Vicat Softening Point >= 300 °C

@Load 5.00 kg
 >= 572 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 0.750 mm
 V-1

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Glow Wire Test 875 °C

@Thickness 1.00 mm
 1610 °F

@Thickness 0.0394 in
 GWIT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Processing Properties Metric English Comments
Melt Temperature 370 - 400 °C
698 - 752 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
 248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa