DuPont Performance Polymers Crastin® HR5315HF NC010 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® HR5315HF NC010 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Crastin® HR5315HF is a 15% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resistance. Developed for USCAR Class 3 and 4 environments.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Filler Content 15 %
15 %
Water Absorption 0.15 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 0.15 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.40 %

@Thickness 1.00 mm,
Temperature 23.0 °C
 0.40 %

@Thickness 0.0394 in,
Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Thickness 2.00 mm
 0.0050 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Thickness 2.00 mm
 0.011 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Index of Compound 18 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 18 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ISO 2039/2
Tensile Strength at Break 40.0 MPa

@Temperature 150 °C
 5800 psi

@Temperature 302 °F
 ISO 527
45.0 MPa

@Temperature 120 °C
 6530 psi

@Temperature 248 °F
 ISO 527
95.0 MPa

@Temperature 23.0 °C
 13800 psi

@Temperature 73.4 °F
 ISO 527
110 MPa

@Temperature -40.0 °C
 16000 psi

@Temperature -40.0 °F
 ISO 527
Tensile Stress 9.67 MPa

@Strain 0.530 %,
Temperature 120 °C
 1400 psi

@Strain 0.530 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
12.1 MPa

@Strain 0.520 %,
Temperature 60.0 °C
 1750 psi

@Strain 0.520 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
15.3 MPa

@Strain 0.310 %,
Temperature 23.0 °C
 2220 psi

@Strain 0.310 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
16.3 MPa

@Strain 1.06 %,
Temperature 120 °C
 2360 psi

@Strain 1.06 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
21.6 MPa

@Strain 1.59 %,
Temperature 120 °C
 3130 psi

@Strain 1.59 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
22.5 MPa

@Strain 1.04 %,
Temperature 60.0 °C
 3260 psi

@Strain 1.04 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
26.0 MPa

@Strain 2.12 %,
Temperature 120 °C
 3770 psi

@Strain 2.12 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
29.2 MPa

@Strain 2.65 %,
Temperature 120 °C
 4240 psi

@Strain 2.65 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
29.5 MPa

@Strain 0.620 %,
Temperature 23.0 °C
 4280 psi

@Strain 0.620 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
31.0 MPa

@Strain 1.56 %,
Temperature 60.0 °C
 4500 psi

@Strain 1.56 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
31.5 MPa

@Strain 3.18 %,
Temperature 120 °C
 4570 psi

@Strain 3.18 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
33.2 MPa

@Strain 3.71 %,
Temperature 120 °C
 4820 psi

@Strain 3.71 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
34.2 MPa

@Strain 4.24 %,
Temperature 120 °C
 4960 psi

@Strain 4.24 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
35.0 MPa

@Strain 4.77 %,
Temperature 120 °C
 5080 psi

@Strain 4.77 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
35.5 MPa

@Strain 5.30 %,
Temperature 120 °C
 5150 psi

@Strain 5.30 %,
Temperature 248 °F
 DAM; ISO 11403-1/-2
37.5 MPa

@Strain 2.08 %,
Temperature 60.0 °C
 5440 psi

@Strain 2.08 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
42.5 MPa

@Strain 0.930 %,
Temperature 23.0 °C
 6160 psi

@Strain 0.930 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
43.3 MPa

@Strain 2.60 %,
Temperature 60.0 °C
 6280 psi

@Strain 2.60 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
47.7 MPa

@Strain 3.12 %,
Temperature 60.0 °C
 6920 psi

@Strain 3.12 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
50.0 MPa

@Strain 3.64 %,
Temperature 60.0 °C
 7250 psi

@Strain 3.64 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
51.2 MPa

@Strain 4.16 %,
Temperature 60.0 °C
 7430 psi

@Strain 4.16 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
51.9 MPa

@Strain 4.68 %,
Temperature 60.0 °C
 7530 psi

@Strain 4.68 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
54.0 MPa

@Strain 1.24 %,
Temperature 23.0 °C
 7830 psi

@Strain 1.24 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
64.2 MPa

@Strain 1.55 %,
Temperature 23.0 °C
 9310 psi

@Strain 1.55 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
72.6 MPa

@Strain 1.86 %,
Temperature 23.0 °C
 10500 psi

@Strain 1.86 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
78.9 MPa

@Strain 2.17 %,
Temperature 23.0 °C
 11400 psi

@Strain 2.17 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
83.4 MPa

@Strain 2.48 %,
Temperature 23.0 °C
 12100 psi

@Strain 2.48 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
86.4 MPa

@Strain 2.79 %,
Temperature 23.0 °C
 12500 psi

@Strain 2.79 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
88.3 MPa

@Strain 3.10 %,
Temperature 23.0 °C
 12800 psi

@Strain 3.10 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
Elongation at Break 2.0 %

@Temperature -40.0 °C
 2.0 %

@Temperature -40.0 °F
 ISO 527
3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 ISO 527
6.0 %

@Temperature 120 °C
 6.0 %

@Temperature 248 °F
 ISO 527
8.0 %

@Temperature 150 °C
 8.0 %

@Temperature 302 °F
 ISO 527
Tensile Modulus 2.10 GPa

@Temperature 150 °C
 305 ksi

@Temperature 302 °F
 ISO 527
2.30 GPa

@Temperature 120 °C
 334 ksi

@Temperature 248 °F
 ISO 527
5.20 GPa

@Temperature 23.0 °C
 754 ksi

@Temperature 73.4 °F
 ISO 527
6.00 GPa

@Temperature -40.0 °C
 870 ksi

@Temperature -40.0 °F
 ISO 527
Flexural Strength 45.0 MPa

@Temperature 150 °C
 6530 psi

@Temperature 302 °F
 ISO 178
60.0 MPa

@Temperature 120 °C
 8700 psi

@Temperature 248 °F
 ISO 178
150 MPa

@Temperature 23.0 °C
 21800 psi

@Temperature 73.4 °F
 ISO 178
170 MPa

@Temperature -40.0 °C
 24700 psi

@Temperature -40.0 °F
 ISO 178
Flexural Modulus 1.70 GPa

@Temperature 150 °C
 247 ksi

@Temperature 302 °F
 ISO 178
2.00 GPa

@Temperature 120 °C
 290 ksi

@Temperature 248 °F
 ISO 178
4.70 GPa

@Temperature 23.0 °C
 682 ksi

@Temperature 73.4 °F
 ISO 178
5.80 GPa

@Temperature -40.0 °C
 841 ksi

@Temperature -40.0 °F
 ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -40.0 °C
 2.86 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature -40.0 °C
 14.3 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1U
40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA