LATI Latamid 66 E21 K/30 PA 66, 30% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 E21 K/30 PA 66, 30% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Toughened. Carbon fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0095 cm/cm
0.0065 - 0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa

@Temperature 150 °C
 10900 psi

@Temperature 302 °F
95.0 MPa

@Temperature 120 °C
 13800 psi

@Temperature 248 °F
110 MPa

@Temperature 90.0 °C
 16000 psi

@Temperature 194 °F
140 MPa

@Temperature 60.0 °C
 20300 psi

@Temperature 140 °F
180 MPa

@Temperature 23.0 °C
 26100 psi

@Temperature 73.4 °F
Elongation at Break 1.8 %

@Temperature 23.0 °C
 1.8 %

@Temperature 73.4 °F
3.0 %

@Temperature 60.0 °C
 3.0 %

@Temperature 140 °F
3.2 %

@Temperature 90.0 °C
 3.2 %

@Temperature 194 °F
4.2 %

@Temperature 120 °C
 4.2 %

@Temperature 248 °F
4.3 %

@Temperature 150 °C
 4.3 %

@Temperature 302 °F
Tensile Modulus 6.00 GPa

@Temperature 150 °C
 870 ksi

@Temperature 302 °F
8.20 GPa

@Temperature 120 °C
 1190 ksi

@Temperature 248 °F
11.7 GPa

@Temperature 90.0 °C
 1700 ksi

@Temperature 194 °F
19.5 GPa

@Temperature 60.0 °C
 2830 ksi

@Temperature 140 °F
20.0 GPa

@Temperature 23.0 °C
 2900 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 200000 ohm-cm
200000 ohm-cm
Surface Resistance 30000 ohm
30000 ohm
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: