LATI Latilon 28D K/20 PC, 20% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | LATI |
| Trade Name | Latilon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latilon 28D K/20 PC, 20% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate (PC) based compound. Carbon fiber. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa @Temperature 120 °C |
9430 psi @Temperature 248 °F |
|
| 90.0 MPa @Temperature 90.0 °C |
13100 psi @Temperature 194 °F |
||
| 110 MPa @Temperature 60.0 °C |
16000 psi @Temperature 140 °F |
||
| 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
||
| Elongation at Break | 1.6 % @Temperature 23.0 °C |
1.6 % @Temperature 73.4 °F |
|
| 1.6 % @Temperature 60.0 °C |
1.6 % @Temperature 140 °F |
||
| 1.6 % @Temperature 90.0 °C |
1.6 % @Temperature 194 °F |
||
| 1.7 % @Temperature 120 °C |
1.7 % @Temperature 248 °F |
||
| Tensile Modulus | 9.40 GPa @Temperature 120 °C |
1360 ksi @Temperature 248 °F |
|
| 10.5 GPa @Temperature 90.0 °C |
1520 ksi @Temperature 194 °F |
||
| 11.5 GPa @Temperature 60.0 °C |
1670 ksi @Temperature 140 °F |
||
| 12.0 GPa @Temperature 23.0 °C |
1740 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 100 - 120 °C | 212 - 248 °F | |
| Drying Temperature | 120 - 130 °C @Time 10800 sec |
248 - 266 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced
- Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced
- SABIC Innovative Plastics NORYL WCD933 PPE-TPE
- ExxonMobil Vistamaxx™ 3000 Propylene-based Elastomer
- ExxonMobil HD 7845.30 MMW Blown Film Resin
- Ashley Polymers Ashlene® 1105 Polycarbonate, 5-7% Glass Reinforced
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 40% Cold Rolled (UNS S30400)
- A. Schulman POLYFORT™ PP 3726
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- SABIC Innovative Plastics Lexan® HFD4412 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved