- DuPont Performance Polymers Minlon® FE6190 BK086 Nylon 66
DuPont Performance Polymers Minlon® FE6190 BK086 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Minlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Minlon® FE6190 BK086 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Minlon® FE6190 BK086 is a 36% mineral/glass reinforced, heat stabilized, black polyamide resin for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | DAM; ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | DAM; ISO 1183 |
| Filler Content | 36 % | 36 % | DAM |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 1.60 mm |
0.0020 in/in @Thickness 0.0630 in |
Flow; DAM |
| 0.0040 cm/cm @Thickness 6.40 mm |
0.0040 in/in @Thickness 0.252 in |
Flow; DAM | |
| 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
Flow; DAM | |
| 0.0080 cm/cm @Thickness 1.60 mm |
0.0080 in/in @Thickness 0.0630 in |
Transverse; DAM | |
| 0.0090 cm/cm @Thickness 3.20 mm |
0.0090 in/in @Thickness 0.126 in |
Transverse; DAM | |
| 0.010 cm/cm @Thickness 6.40 mm |
0.010 in/in @Thickness 0.252 in |
Transverse; DAM | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa @Temperature 23.0 °C |
10900 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Tensile Strength | 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
| Elongation at Break | 2.2 % @Temperature 23.0 °C |
2.2 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
DAM; ASTM D638 | |
| 3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 6.20 GPa @Temperature 23.0 °C |
899 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 9.00 GPa @Temperature 23.0 °C |
1310 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Strength | 159 MPa @Temperature 23.0 °C |
23100 psi @Temperature 73.4 °F |
DAM; ASTM D790 |
| Flexural Modulus | 6.90 GPa @Temperature 23.0 °C |
1000 ksi @Temperature 73.4 °F |
DAM; ASTM D790 |
| 8.00 GPa @Temperature 23.0 °C |
1160 ksi @Temperature 73.4 °F |
DAM; ISO 178 | |
| Izod Impact, Notched | 0.430 J/cm @Temperature 23.0 °C |
0.806 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
50%RH; ASTM D256 | |
| Izod Impact, Unnotched | 4.80 J/cm @Temperature 23.0 °C |
8.99 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -40.0 °C |
1.19 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
45.0 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 81.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
45.0 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 263 °C | 505 °F | DAM; ASTM D3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | DAM; ASTM D648 |
| 255 °C | 491 °F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DAM; ISO 75-1/-2 |
| 235 °C | 455 °F | DAM; ASTM D648 | |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; UL94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 °C | 563 °F | DAM; Optimum |
| 285 - 305 °C | 545 - 581 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Glass/Mineral | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66-I(MD+GF)36< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass/Mineral Reinforced Resins | DAM |
| Low Warp Resins | DAM | |
| Resin Identification | PA66-I(MD+GF)36 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- Outokumpu SAF 2507® Duplex Stainless Steel
- SABIC Innovative Plastics XYLEX X8303CL PC+POLYESTER (Europe-Africa-Middle East)
- Samsung Cheil Industries Starex® VB-4921 ABS, Glass Filled FR
- Arkema Group ORGASOL® 2002 ES 4 Nat 3 Polyamide 12
- California Fine Wire Nickel Alloy 99 Nickel Alloy
- 3M Headlap Roofing Granule (Pittsboro)
- 3M Nextel™ AF-11 Industrial Woven Fabric 312
- ExxonMobil Paxon™ EA55-003 Blow Molding Resin
- DuPont Performance Polymers Sorona® 3301V BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
Copyright © lookpolymers.com All Rights Reserved