LATI Latamid 66 H2 G/50-GWHF1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/50-GWHF1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. improved G.W.F.I. compared to standard product.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.012 cm/cm
0.0080 - 0.012 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa

@Temperature 150 °C
 11600 psi

@Temperature 302 °F
90.0 MPa

@Temperature 120 °C
 13100 psi

@Temperature 248 °F
110 MPa

@Temperature 90.0 °C
 16000 psi

@Temperature 194 °F
150 MPa

@Temperature 60.0 °C
 21800 psi

@Temperature 140 °F
205 MPa

@Temperature 23.0 °C
 29700 psi

@Temperature 73.4 °F
Elongation at Break 2.2 %

@Temperature 23.0 °C
 2.2 %

@Temperature 73.4 °F
3.0 %

@Temperature 60.0 °C
 3.0 %

@Temperature 140 °F
3.8 %

@Temperature 90.0 °C
 3.8 %

@Temperature 194 °F
4.1 %

@Temperature 120 °C
 4.1 %

@Temperature 248 °F
4.4 %

@Temperature 150 °C
 4.4 %

@Temperature 302 °F
Tensile Modulus 5.00 GPa

@Temperature 150 °C
 725 ksi

@Temperature 302 °F
6.00 GPa

@Temperature 120 °C
 870 ksi

@Temperature 248 °F
6.50 GPa

@Temperature 90.0 °C
 943 ksi

@Temperature 194 °F
11.0 GPa

@Temperature 60.0 °C
 1600 ksi

@Temperature 140 °F
16.5 GPa

@Temperature 23.0 °C
 2390 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Oxygen Index 27 %
27 %
Glow Wire Test 800 °C

@Thickness 1.00 mm
 1470 °F

@Thickness 0.0394 in
 GWFI/GWT
800 °C

@Thickness 2.00 mm
 1470 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa