DuPont Performance Polymers Zytel® BM70G15HSLR BK537 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® BM70G15HSLR BK537 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® BM70G15HSLR BK537 is a 15% glass fiber reinforced polyamide 66 for blow molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | DAM; ISO 1183 |
| Filler Content | 15 % | 15 % | DAM |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm | 0.0039 in/in | DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C |
8700 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 4.5 % @Temperature 23.0 °C |
4.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 21 % @Temperature 23.0 °C |
21 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 3.50 GPa @Temperature 23.0 °C |
508 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 5.40 GPa @Temperature 23.0 °C |
783 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Charpy Impact Unnotched | 7.10 J/cm² @Temperature 23.0 °C |
33.8 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU |
| 7.10 J/cm² @Temperature 23.0 °C |
33.8 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum; Blow Molding |
| 285 - 305 °C | 545 - 581 °F | DAM; Blow Molding | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | DAM; Blow Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | DAM; Blow Molding |
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Blow Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Glass fiber reinforcement | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Preliminary Data | DAM |
| Part Marking Code | >PA66-IGF15< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| Processing Method | Blow Molding | DAM |
| Product Category | Blow Moldable Resins | DAM |
| Glass Reinforced Resins | DAM | |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA66-IGF15 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- RheTech Products HP521-372 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 110D Medium Dark Pewter
- Nye Lubricants PML-W-10 Grease
- Momentive Performance Materials Siloprenâ„¢ LSR 4640 Liquid Silicone Rubber - Healthcare
- Sinotek Materials ZSLG98 High Carbon Graphite
- Borealis Borecene™ RM8343PL Linear Polyethylene for Rotational Molding
- Borealis Daplen™ EE260AI Polypropylene TPO Compound
- Covestro Makrolon® ET UV540 Polycarbonate
- 3M Fluorinert™ FC-3284 Electronic Liquid
- Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Conditioned, 35% Glass Filled
Copyright © lookpolymers.com All Rights Reserved